Multilayer ceramic capacitor

ABSTRACT

A multilayer ceramic capacitor includes a body and first and second outer electrodes. The body includes a multilayer unit with ceramic dielectric layers and conductive layers alternately stacked on each other. The body is sectioned into a thickness-direction inner layer section that includes the multilayer unit and thickness-direction first and second outer layer sections that sandwich the thickness-direction inner layer section therebetween. A dimension of the thickness-direction second outer layer section is greater than a dimension of the thickness-direction first outer layer section. A conductive layer closest to a first principal surface and a conductive layer closest to a second principal surface are first and second outermost conductive layers, respectively. A curving amount of an extension portion of the second outermost conductive layer is greater than that of an extension portion of the first outermost conductive layer.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a multilayer ceramic capacitor, and a multilayer ceramic capacitor array including a multilayer ceramic capacitor.

2. Description of the Related Art

Generally, a capacitor device includes a body constituted by alternately stacking inner electrode layers and dielectric layers and outer electrodes disposed on the outer surfaces of the body. In a multilayer ceramic capacitor, the dielectric layers are constituted by a ceramic dielectric material.

Generally, the body of a multilayer ceramic capacitor is formed as follows. The body contains a multilayer unit having a substantially rectangular parallelepiped shape and formed by alternately and densely stacking a plurality of conductive layers, which serve as inner electrode layers, and a plurality of ceramic dielectric layers. Outer layer sections constituted by ceramic dielectric layers and outer layer sections constituted by ceramic dielectric layers and a relatively small number of conductive layers disposed within the ceramic dielectric layers cover the multilayer unit.

In the above-described multilayer ceramic capacitor, the occurrence of cracks in the above-described ceramic dielectric layers may be observed. The occurrence of cracks reduces the reliability of a multilayer ceramic capacitor as a product or decreases the yield in a manufacturing process.

An example of a technique for reducing the occurrence of cracks in a multilayer ceramic capacitor is disclosed in Japanese Unexamined Patent Application Publication No. 2012-248581. In this multilayer ceramic capacitor, a pair of outer layer sections constituted by ceramic dielectric layers that sandwich the above-described multilayer unit therebetween in the stacking direction is provided. In this pair of outer layer sections, one outer layer section that defines the principal surface of the multilayer unit to be mounted on a wiring board is thicker than the other outer layer section.

In this multilayer ceramic capacitor, it is possible to reduce the occurrence of cracks caused by an external stress which is applied to the multilayer ceramic capacitor when the wiring board having the multilayer ceramic capacitor mounted thereon is deflected due to an external force.

However, as a result of conducting an extensive study, the present inventors have discovered the following fact concerning the above-described multilayer ceramic capacitor. If the thickness of the above-described other outer layer section is increased or if the thickness of the above-described multilayer unit is increased, cracks occur at the boundary between the multilayer unit and the outer layer section when the body of the multilayer ceramic capacitor is subjected to firing. Unlike the above-described cracks due to an external stress, this type of crack may occur due to an internal stress produced by the difference in the coefficients of thermal shrinkage between the ceramic dielectric layers and the conductive layers when the body of the multilayer ceramic capacitor is subjected to firing.

SUMMARY OF THE INVENTION

Accordingly, preferred embodiments of the present invention provide a multilayer ceramic capacitor in which cracks caused by an internal stress produced by a difference in coefficients of thermal shrinkage of a ceramic dielectric layer and a conductive layer are significantly reduced or prevented, and a multilayer ceramic capacitor array including this multilayer ceramic capacitor and a multilayer ceramic capacitor mount body including this multilayer ceramic capacitor.

According to a preferred embodiment of the present invention, a multilayer ceramic capacitor includes a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction, and a plurality of outer electrodes disposed on portions of the body, wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction, the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface, some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode, the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween, the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections, a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction, one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface, one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface, and an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer.

According to another preferred embodiment of the present invention, a multilayer ceramic capacitor includes a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction, and a plurality of outer electrodes disposed on portions of the body, wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction, the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface, some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode, the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween, the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections, a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction, one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface, one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface, an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer, the second outermost conductive layer is an ineffective conductive layer, and the amount of the inclination of the second outermost conductive layer is larger than a thickness of the ceramic dielectric layer adjacent to the second outermost conductive layer in the multilayer unit.

According to yet another preferred embodiment of the present invention, a multilayer ceramic capacitor includes a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction, and a plurality of outer electrodes disposed on portions of the body, wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction, the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface, some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode, the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween, the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections, a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction, one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface, one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface, an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer, the conductive layer nearest to the first principal surface is a first conductive layer, a distance between the multilayer unit and the first side surface through the first conductive layer in the width direction and a distance between the multilayer unit and the second side surface through the first conductive layer in the width direction are greater than a dimension of the thickness-direction first outer layer section in the thickness direction, and a distance between the multilayer unit and the first end surface through the first conductive layer in the length direction and a distance between the multilayer unit and the second end surface through the first conductive layer in the length direction are greater than a dimension of the thickness-direction first outer layer section in the thickness direction

In any of the above-described multilayer ceramic capacitors according to various preferred embodiments of the present invention, a dimension of the second outermost conductive layer in the width direction is smaller than a dimension of a third conductive layer in the width direction which is disposed closest to a center of the multilayer unit in the thickness direction.

In any of the above-described multilayer ceramic capacitors according to various preferred embodiments of the present invention, the ceramic dielectric layers included in the thickness-direction inner layer section and the thickness-direction first and second outer layer sections contains barium titanate and Si, the thickness-direction second outer layer section includes an outer portion which defines the second principal surface and an inner portion disposed between the thickness-direction inner layer section and the outer portion, a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the outer portion is higher than a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the inner portion, and a boundary portion disposed between the outer portion and the inner portion has a larger Si content than the outer portion.

In any of the above-described multilayer ceramic capacitors according to various preferred embodiments of the present invention, the ceramic dielectric layers included in the multilayer unit have a higher composition ratio of rare earth element to Ti than the outer portion, and the inner portion has a higher composition ratio of Mn to Ti than that of the outer portion.

In the present application, the term “composition ratio of Si to Ti” indicates a value of Si mol/Ti mol, the term “composition ratio of rare earth element to Ti” indicates a value of rare earth element mol/Ti mol, and the term “composition ratio of Mn to Ti” indicates a value of Mn mol/Ti mol, and Si content can be recognized by element mapping, for example.

In any of the above-described multilayer ceramic capacitors according to various preferred embodiments of the present invention, a dimension of the outer portion in the thickness direction preferably is greater than a dimension of the inner portion in the thickness direction.

In any of the above-described multilayer ceramic capacitors according to various preferred embodiments of the present invention, a dimension of the multilayer unit in the thickness direction preferably is greater than a dimension of the multilayer unit in the width direction, and a dimension of the body in the thickness direction preferably is greater than a dimension of the body in the width direction.

According to yet another preferred embodiment of the present invention, a multilayer ceramic capacitor array includes a plurality of multilayer ceramic capacitors according to one of various preferred embodiments of the present invention, and a package including an elongated carrier tape having a plurality of recessed portions disposed apart from each other and a cover tape that is attached to the elongated carrier tape so as to cover the plurality of recessed portions. The plurality of multilayer ceramic capacitors are stored in the plurality of respective recessed portions such that the second principal surfaces of the plurality of multilayer ceramic capacitors face bottom portions of the plurality of respective recessed portions.

According to another preferred embodiment of the present invention, a multilayer ceramic capacitor mount body includes a plurality of multilayer ceramic capacitors according to one of various preferred embodiments of the present invention; and a mounting member on which the plurality of multilayer ceramic capacitors are mounted. The plurality of multilayer ceramic capacitors are mounted on the mounting member such that the second principal surfaces of the plurality of multilayer ceramic capacitors face the mounting member.

According to various preferred embodiments of the present invention, it is possible to provide a multilayer ceramic capacitor in which the occurrence of cracks caused by an internal stress produced by the difference in the coefficients of thermal shrinkage between a ceramic dielectric layer and a conductive layer is significantly reduced or prevented, and a multilayer ceramic capacitor array including this multilayer ceramic capacitor and a multilayer ceramic capacitor mount body including this multilayer ceramic capacitor.

The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic perspective view illustrating a multilayer ceramic capacitor according to a first preferred embodiment of the present invention.

FIGS. 2 and 3 are schematic sectional views taken along lines II-II and III-III, respectively, of FIG. 1.

FIGS. 4 and 5 are enlarged sectional views of regions IV and V, respectively, shown in FIG. 2.

FIG. 6 illustrates the dimensional relationships among specific inner electrode layers in a predetermined cross section of the body of the multilayer ceramic capacitor of the first preferred embodiment of the present invention.

FIGS. 7A and 7B illustrate the areal relationships among specific inner electrode layers in a predetermined cross section of the body of the multilayer ceramic capacitor of the first preferred embodiment of the present invention.

FIG. 8 is a flowchart illustrating a manufacturing flow for the multilayer ceramic capacitor shown in FIG. 1.

FIG. 9 is an exploded perspective view illustrating a multilayer structure of a set of base sheets, which define a body of the multilayer ceramic capacitor shown in FIG. 1.

FIGS. 10A through 11B are schematic sectional views illustrating a step of fixing a set of material sheets with pressure in the manufacturing flow shown in FIG. 8.

FIG. 12 is a schematic sectional view illustrating a multilayer ceramic capacitor mount body of the first preferred embodiment of the present invention.

FIG. 13 is a plan view illustrating a multilayer ceramic capacitor array of the first preferred embodiment of the present invention.

FIG. 14 is a schematic sectional view taken along line XIV-XIV of FIG. 13.

FIG. 15 is a schematic perspective view illustrating a multilayer ceramic capacitor according to a second preferred embodiment of the present invention.

FIGS. 16 and 17 are schematic sectional views taken along lines XVI-XVI and XVII-XVII, respectively, of FIG. 15.

FIG. 18 is a table illustrating design conditions and evaluation results for multilayer ceramic capacitors of examples 1 through 21 in a first verification test.

FIG. 19 is a table illustrating design conditions and evaluation results for multilayer ceramic capacitors of examples 22 through 25 in a second verification test.

FIG. 20 is a schematic view illustrating a method for deflecting a wiring board having a multilayer ceramic capacitor mounted thereon in the second verification test.

FIG. 21 illustrates an example of an enlarged image of a cross section of a multilayer ceramic capacitor observed with a scanning electron microscope (SEM).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS First Preferred Embodiment

FIG. 1 is a schematic perspective view illustrating a multilayer ceramic capacitor 1A according to a first preferred embodiment of the present invention. FIGS. 2 and 3 are schematic sectional views taken along lines II-II and III-III, respectively, of FIG. 1. FIGS. 4 and 5 are enlarged sectional views of regions IV and V, respectively, showing FIG. 2. The configuration of the multilayer ceramic capacitor 1A of the first preferred embodiment will first be described below with reference to FIGS. 1 through 5.

As shown in FIGS. 1 through 3, the multilayer ceramic capacitor 1A is an electronic component preferably having a rectangular or substantially rectangular parallelepiped shape and including a body 2 and first and second outer electrodes 5 a and 5 b, which define a pair of outer electrodes.

As shown in FIGS. 2 and 3, the body 2 preferably has a rectangular or substantially rectangular parallelepiped shape and includes ceramic dielectric layers 3 and inner electrode layers 4 alternately stacked on each other in a predetermined direction. The inner electrode layers 4 define and serve as conductive layers. The term “rectangular parallelepiped” includes a rectangular parallelepiped having a rounded portion at a corner or a ridge of the body 2 and a rectangular parallelepiped having a step portion or uneven portion, which is negligible as a whole, on the surface of the body 2.

The ceramic dielectric layers 3 contain a perovskite compound expressed by ABO₃ (“A” contains Ba and “B” contains Ti) as a principal component. A typical example of a perovskite compound expressed by ABO₃ is barium titanate (BaTiO₃).

The ceramic dielectric layers 3 contain Si as a secondary component. Si is contained in the ceramic dielectric layers 3 by adding a Si compound, such as glass or SiO₂, to a perovskite compound expressed by ABO₃. Another compound, such as a Mn compound, an Mg compound, a Co compound, a Ni compound, or a rare earth compound, may be added to a perovskite compound expressed by ABO₃.

In the first preferred embodiment, the principal component of the ceramic dielectric material for the ceramic dielectric layers 3 is not restricted to a perovskite compound expressed by ABO₃ (“A” contains Ba and “B” contains Ti). Another ceramic dielectric material having a high dielectric constant containing, for example, calcium titanate, strontium titanate, or calcium zirconate as a principal component, may be used.

As a material for the inner electrode layers 4, a metal, such as Ni, Cu, Ag, Pd, or Au, or an alloy containing at least one of such metals (for example, an alloy of Ag and Pd) may be used, for example. The thickness of each inner electrode layer 4 after the body 2 has been fired is preferably about 0.3 μm to about 2 μm, for example.

The body 2 is preferably fabricated in the following manner. A plurality of material sheets, that is, a plurality of ceramic green sheets, which will form the ceramic dielectric layers 3, on which conductor patterns, which will form the inner electrode layers 4, are printed, are first prepared. These material sheets are stacked on and pressed against each other so as to form a mother block. Then, the mother block is cut into a plurality of chips, and they are fired. Each of the plurality of chips serves as the body 2. Details of this fabrication process will be discussed later.

As shown in FIGS. 1 through 3, the first and second outer electrodes 5 a and 5 b are disposed separately from each other such that they cover outer surfaces of the body 2 which are positioned at both end portions thereof in a predetermined direction. The first and second outer electrodes 5 a and 5 b each include a conductive film.

The first and second outer electrodes 5 a and 5 b each include a foundation layer which covers the above-described end portions of the body 2 and a plated layer which covers the foundation layer. As a material for the foundation layer, a metal, such as Ni, Cu, Ag, Pd, or Au, or an alloy containing at least one of such metals (for example, an alloy of Ag and Pd) may be used, for example. The thickness of the foundation layer is preferably about 10 μm to about 50 μm, for example.

The foundation layer may be formed by burning a conductor paste applied to the above-described end portions of the body 2 which has been fired. Alternatively, the foundation layer may be formed by firing, together with the inner electrode layers 4, a conductor paste applied to the above-described end portions of the body 2 which has not been fired. Alternatively, the foundation layer may be formed by plating the above-described end portions of the body 2 or by curing a thermosetting resin containing a metal applied to the end portions of the body 2.

If the foundation layer contains a resin, it is possible to reduce a load on the body 2 caused by an external stress which is produced when a mounting member (for example, a wiring board 101, which will be discussed later) having the multilayer ceramic capacitor 1A mounted thereon is deflected due to an external force. This makes it possible to reduce the occurrence of cracks in the body 2.

As a material for the plated layer, a metal, such as Ni, Sn, Cu, Ag, Pd, or Au, or an alloy containing at least one of such metals (for example, an alloy of Ag and Pd) may be used, for example.

The plated layer may be constituted by a plurality of layers, for example. In this case, the plated layer is preferably a two-layer structure in which a Sn plated layer is provided on a Ni plated layer. In this case, the Ni plated layer functions as a solder barrier layer, while the Sn plated layer improves solder wettability. The thickness of one plated layer is preferably about 1.0 μm to about 10 μm, for example.

As shown in FIG. 2, if it is assumed that two inner electrode layers 4 adjacent to each other with a ceramic dielectric layer 3 therebetween in the stacking direction define a pair, one inner electrode layer 4 is connected to the first outer electrode 5 a via a first extension portion 4 c 1 within the multilayer ceramic capacitor 1A, while the other inner electrode layer 4 is connected to the second outer electrode 5 b via a second extension portion 4 c 2 within the multilayer ceramic capacitor 1A. The plurality of inner electrode layers 4 preferably are all rectangular or substantially rectangular, as viewed from above.

In the multilayer ceramic capacitor 1A of the first preferred embodiment configured as described above, a plurality of capacitor elements are electrically connected in parallel between the first and second outer electrodes 5 a and 5 b. The first extension portion 4 c 1 is a portion positioned between an effective portion of the inner electrode layers 4 (that is, an area where a plurality of inner electrode layers 4 are stacked in the stacking direction) and the first outer electrode 5 a, while the second extension portion 4 c 2 is a portion positioned between the effective portion of the inner electrode layers 4 and the second outer electrode 5 b. The effective portion of the inner electrode layers 4 will be discussed later.

In the first preferred embodiment, preferably all the conductive layers, that is, all the inner electrode layers 4, inside the body 2 are connected to one of the first and second outer electrodes 5 a and 5 b. However, the multilayer ceramic capacitor 1A may be configured in a different manner as long as at least some of the plurality of conductive layers are connected to the first outer electrode 5 a and at least some of the remaining conductive layers are connected to the second outer electrode 5 b. That is, there may be some conductive layers that are neither connected to the first outer electrode 5 a nor the second outer electrode 5 b.

In this case, if a conductive layer connected to the first outer electrode 5 a opposes a conductive layer connected to the second outer electrode 5 b via an associated ceramic dielectric layer 3 so as to contribute to the generation of electrostatic capacitance, these conductive layers are effective conductive layers. In contrast, among the above-described conductive layers, if some conductive layers do not contribute to the generation of electrostatic capacitance, they are ineffective conductive layers. That is, even if a conductive layer is connected to one of the first outer electrode 5 a and the second outer electrode 5 b, but if none of the conductive layers opposing such a conductive layer via the ceramic dielectric layer 3 are connected to the other one of the second outer electrode 5 b and the first outer electrode 5 a, this conductive layer is an ineffective conductive layer. In the first preferred embodiment, the plurality of conductive layers preferably are all alternately connected to the first outer electrode 5 a and the second outer electrode 5 b, and thus, they are all effective conductive layers without any ineffective conductive layers, for example.

In the first preferred embodiment, a first conductive layer, which is the conductive layer disposed closest to a first principal surface 2 a 1 among a plurality of conductive layers, coincides with a first outermost layer, which is the conductive layer disposed closest to the first principal surface 2 a 1 among the plurality of conductive layers connected to either one of the first and second outer electrodes 5 a and 5 b (such a conductive layer is denoted by 4 a in the drawings). A second conductive layer, which is the conductive layer disposed closest to a second principal surface 2 a 2 among the plurality of conductive layers, coincides with a second outermost layer, which is the conductive layer disposed closest to the second principal surface 2 a 2 among a plurality of conductive layers connected to either one of the first and second outer electrodes 5 a and 5 b (such a conductive layer is denoted by 4 b in the drawings). The first and second conductive layers and the first and second outermost layers will be discussed later.

However, it is not always necessary that the first conductive layer and the first outermost layer coincide with each other, nor is it always necessary that the second conductive layer and the second outermost layer coincide with each other. That is, if the first conductive layer is connected neither to the first outer electrode 5 a nor the second outer electrode 5 b, it means that the first outermost layer is positioned closer to the second principal surface 2 a 2 than the first conductive layer, and if the second conductive layer is connected neither to the first outer electrode 5 a nor the second outer electrode 5 b, it means that the second outermost layer is positioned closer to the first principal surface 2 a 1 than the second conductive layer.

Note that it does not matter whether the first and the second outermost layers are effective conductive layers or ineffective conductive layers.

As shown in FIGS. 2 and 3, in the multilayer ceramic capacitor 1A of the first preferred embodiment, the inner electrode layers 4 other than those defining the first and second extension portions 4 c 1 and 4 c 2 define the effective portion that determines the electrostatic capacitance of the multilayer ceramic capacitor 1A. The effective portion of the inner electrode layers 4 and the ceramic dielectric layers 3 positioned between the inner electrode layers 4 defines a multilayer unit 10. The multilayer unit 10 is formed preferably by densely stacking the ceramic dielectric layers 3 and the inner electrode layers 4 in the thickness direction, for example.

By referring to FIGS. 1 through 3, as the orientations of the multilayer ceramic capacitor 1A, the stacking direction of the ceramic dielectric layers 3 and the inner electrode layers 4 will be defined as a thickness direction T, the direction in which the first and second outer electrodes 5 a and 5 b are arranged side by side perpendicular to the thickness direction T is defined as a length direction L, and the direction perpendicular to both of the thickness direction T and the length direction L is defined as a width direction W. In the following description, these terms will be used.

By referring to FIGS. 2 and 3, among six outer surfaces of the body 2, a pair of outer surfaces opposing each other in the thickness direction T will be defined as first and second principal surfaces 2 a 1 and 2 a 2, a pair of outer surfaces opposing each other in the length direction L will be defined as first and second end surfaces 2 b 1 and 2 b 2, and a pair of outer surfaces opposing each other in the width direction W will be defined as first and second side surfaces 2 c 1 and 2 c 2. In the following description, these terms will be used.

As shown in FIGS. 1 through 3, the first and second outer electrodes 5 a and 5 b are disposed such that they cover outer surfaces of the body 2 which are positioned in the length direction L. More specifically, the first outer electrode 5 a is disposed such that it covers the first end surface 2 b 1 and also covers portions of the first and second principal surfaces 2 a 1 and 2 a 2 and the first and second side surfaces 2 c 1 and 2 c 2 positioned closer to the first end surface 2 b 1, while the second outer electrode 5 b is disposed such that it covers the second end surface 2 b 2 and also covers portions of the first and second principal surfaces 2 a 1 and 2 a 2 and the first and second side surfaces 2 c 1 and 2 c 2 positioned closer to the second end surface 2 b 2.

As shown in FIGS. 2 and 3, the body 2 is sectioned in the thickness direction T into a thickness-direction inner layer section 6 a and thickness-direction first and second outer layer sections 6 b 1 and 6 b 2.

The thickness-direction inner layer section 6 a includes the multilayer unit 10 and is constituted by the inner electrode layers 4 and ceramic dielectric layers 3. The inner electrode layers 4 defining the thickness-direction inner layer section 6 a include the inner electrode layers 4 contained in the multilayer unit 10, the inner electrode layers 4 defining the first extension portion 4 c 1 which extends from some of the inner electrode layers 4 contained in the multilayer unit 10 toward the first end surface 2 b 1 so as to be connected to the first outer electrode 5 a, and the inner electrode layers 4 defining the second extension portion 4 c 2 which extends from the remaining inner electrode layers 4 contained in the multilayer unit 10 toward the second end surface 2 b 2 so as to be connected to the second outer electrode 5 b.

The thickness-direction first outer layer section 6 b 1 is constituted by a ceramic dielectric layer 3 and does not include any inner electrode layer 4. The thickness-direction first outer layer section 6 b 1 covers the surface of the thickness-direction inner layer section 6 a closer to the first principal surface 2 a 1 so as to define the first principal surface 2 a 1 of the body 2.

The thickness-direction second outer layer section 6 b 2 is constituted by a ceramic dielectric layer 3 and does not include any inner electrode layer 4. The thickness-direction second outer layer section 6 b 2 covers the surface of the thickness-direction inner layer section 6 a closer to the second principal surface 2 a 2 so as to define the second principal surface 2 a 2 of the body 2.

With this configuration, the thickness-direction inner layer section 6 a is sandwiched between the thickness-direction first and second outer layer sections 6 b 1 and 6 b 2 in the thickness direction T. Among the inner electrode layers 4 contained in the thickness-direction inner layer section 6 a, the first conductive layer 4 a disposed closest to the first principal surface 2 a 1 is disposed adjacent to the ceramic dielectric layer 3 defining the thickness-direction first outer layer section 6 b 1. Among the inner electrode layers 4 contained in the thickness-direction inner layer section 6 a, the second conductive layer 4 b disposed closest to the second principal surface 2 a 2 is disposed adjacent to the ceramic dielectric layer 3 defining the thickness-direction second outer layer section 6 b 2.

As shown in FIG. 2, the body 2 is sectioned in the length direction L into a length-direction inner layer section 7 a and length-direction first and second outer layer sections 7 b 1 and 7 b 2.

The length-direction inner layer section 7 a includes the multilayer unit 10 and is constituted by the inner electrode layers 4 and ceramic dielectric layers 3. The inner electrode layers 4 defining the length-direction inner layer section 7 a are constituted only by the inner electrode layers 4 contained in the multilayer unit 10.

The length-direction first outer layer section 7 b 1 is constituted by the inner electrode layers 4 defining the first extension portion 4 c 1 and portions of the ceramic dielectric layers 3. The length-direction first outer layer section 7 b 1 covers the surface of the length-direction inner layer section 7 a closer to the first end surface 2 b 1 so as to define the first end surface 2 b 1 of the body 2.

The length-direction second outer layer section 7 b 2 is constituted by the inner electrode layers 4 defining the second extension portion 4 c 2 and portions of the ceramic dielectric layers 3. The length-direction second outer layer section 7 b 2 covers the surface of the length-direction inner layer section 7 a closer to the second end surface 2 b 2 so as to define the second end surface 2 b 2 of the body 2.

With this configuration, the length-direction inner layer section 7 a is sandwiched between the length-direction first and second outer layer sections 7 b 1 and 7 b 2 in the length direction L.

As shown in FIG. 3, the body 2 is sectioned in the width direction W into a width-direction inner layer section 8 a and width-direction first and second outer layer sections 8 b 1 and 8 b 2.

The width-direction inner layer section 8 a includes the multilayer unit 10 and is constituted by the inner electrode layers 4 and ceramic dielectric layers 3. The inner electrode layers 4 defining the width-direction inner layer section 8 a include the inner electrode layers 4 contained in the multilayer unit 10 and the inner electrode layers 4 defining the first and second extension portions 4 c 1 and 4 c 2.

The width-direction first outer layer section 8 b 1 is constituted by a ceramic dielectric layer 3 and does not include any inner electrode layer 4. The width-direction first outer layer section 8 b 1 covers the surface of the width-direction inner layer section 8 a closer to the first side surface 2 c 1 so as to define the first side surface 2 c 1 of the body 2.

The width-direction second outer layer section 8 b 2 is constituted by a ceramic dielectric layer 3 and does not include any inner electrode layer 4. The width-direction second outer layer section 8 b 2 covers the surface of the width-direction inner layer section 8 a closer to the second side surface 2 c 2 so as to define the second side surface 2 c 2 of the body 2.

With this configuration, the width-direction inner layer section 8 a is sandwiched between the width-direction first and second outer layer sections 8 b 1 and 8 b 2 in the width direction W.

In this manner, in the multilayer ceramic capacitor 1A of the first preferred embodiment, the multilayer unit 10 formed preferably by alternately and densely stacking the plurality of inner electrode layers 4 and the plurality of ceramic dielectric layers 3 is contained in the body 2. Outer layer sections constituted by ceramic dielectric layers 3 (that is, the thickness-direction first and second outer layer sections 6 b 1 and 6 b 2 and the width-direction first and second outer layer sections 8 b 1 and 8 b 2) and outer layer sections constituted by portions of ceramic dielectric layers 3 and portions of a relatively small number of inner electrode layers 4 which are disposed between the ceramic dielectric layers 3 (that is, the length-direction first and second outer layer sections 7 b 1 and 7 b 2) are disposed such that they cover the multilayer unit 10. With this arrangement, the body 2 is provided.

As shown in FIG. 3, in the multilayer ceramic capacitor 1A of the first preferred embodiment, a dimension T1 of the multilayer unit 10 in the thickness direction T is preferably greater than a dimension W1 of the multilayer unit 10 in the width direction W (T1>W1). In the multilayer ceramic capacitor 1A of the first preferred embodiment, the dimension of the multilayer unit 10 in the width direction W is not uniform with respect to the thickness direction T, which will be discussed later. Accordingly, the above-described dimension W1 of the multilayer unit 10 in the width direction W is determined by the largest dimension of a largest-width inner electrode layer 4 d, which defines and serves as a fourth conductive layer, among the plurality of inner electrode layers 4.

With this configuration, it is possible to provide a large multilayer unit 10 without increasing the dimension W1 in the width direction W. This makes it possible to increase the number of ceramic dielectric layers 3 and inner electrode layers to be stacked in the thickness direction T. Thus, without increasing the size of the multilayer ceramic capacitor 1A in the width direction W (in other words, without increasing the area required for mounting the multilayer ceramic capacitor 1A), the electrostatic capacitance of the multilayer ceramic capacitor 1A is increased.

As shown in FIG. 2, in the multilayer ceramic capacitor 1A of the first preferred embodiment, a dimension L1 of the multilayer unit 10 in the length direction L is preferably greater than the dimension T1 of the multilayer unit 10 in the thickness direction T (L1>T1). The reason for this is as follows. It is necessary to separate the first and second outer electrodes 5 a and 5 b from each other by a considerable distance in the length direction L to secure insulation characteristics therebetween, which inevitably increases the dimension L1 of the multilayer unit 10 in the length direction L. Even if the number of ceramic dielectric layers 3 and inner electrode layers 4 is decreased in the thickness direction T for the sake of the increased dimension L of the multilayer unit 10 in the length direction L, a considerable amount of electrostatic capacitance is secured.

As shown in FIGS. 2 and 3, in the multilayer ceramic capacitor 1A of the first preferred embodiment, a dimension T0 of the body 2 in the thickness direction T is preferably greater than a dimension W0 of the body 2 in the width direction W (T0>W0), and also, a dimension L0 of the body 2 in the length direction L is preferably greater than the dimension T0 of the body 2 in the thickness direction T (L0>T0). The reason for setting the relationships among the dimensions of the body 2 in this manner is to reduce the size of the multilayer ceramic capacitor 1A to a minimal level to implement high-density mounting. A largest possible size of the multilayer unit 10 is first secured, and then, it is necessary to minimize the sizes of various outer layer sections (that is, the above-described thickness-direction first and second outer layer sections 6 b 1 and 6 b 2, length-direction first and second outer layer sections 7 b 1 and 7 b 2, and width-direction first and second outer layer sections 8 b 1 and 8 b 2). To implement this, the relationships among the outer dimensions of the body 2 are preferably the same as those of the multilayer unit 10.

As shown in FIGS. 2 and 3, a dimension t2 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is greater than a dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T (t2>t1). With this configuration, the multilayer ceramic capacitor 1A can be mounted on a mounting member, such as a wiring board, such that the second principal surface 2 a 2 defined by the thickness-direction second outer layer section 6 b 2 faces the mounting member. Thus, even if the mounting member is deflected due to an external force, it is possible to significantly reduce or prevent the occurrence of cracks caused by an external stress applied to the multilayer ceramic capacitor 1A.

As discussed above, generally, in a multilayer ceramic capacitor, a crack may be produced in a ceramic dielectric layer because an internal stress produced by the difference in the coefficients of thermal shrinkage between ceramic dielectric layers and conductive layers acts as a shear stress on the ceramic dielectric layer.

Concerning the length direction, this type of crack is likely to be produced mostly at a boundary between a length-direction inner layer section and a length-direction first or second outer layer section, in which case, a crack is produced in an area starting from a longitudinal end portion of the multilayer unit to the surface of the body near this longitudinal end portion. Concerning the length direction, in particular, this type of crack is also likely to be produced at a boundary between an extension portion of a conductive layer contained in the length-direction first or second outer layer section and a ceramic dielectric layer adjacent to this extension portion. This crack is also referred to as “interlayer delamination”.

Concerning the width direction, this type of crack is likely to be produced mostly at a boundary between a width-direction inner layer section and a width-direction first or second outer layer section, in which case, a crack is produced in an area starting from a widthwise end portion of the multilayer unit to the surface of the body near this widthwise end portion.

These cracks are particularly produced around a boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2 when the dimension t2 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is greater than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T, as in the case of the first preferred embodiment of the present invention.

As a result of conducting an extensive study, the present inventors have conceived that the occurrence of such a crack caused by an internal stress produced by the difference in the coefficients of thermal shrinkage between ceramic dielectric layers and conductive layers is capable of being reduced or prevented by configuring the first and second extension portions in the length direction to be a specific configuration, and have discovered that the following configuration of the first and second extension portions is effective to significantly reduce or prevent such cracks from occurring.

As shown in FIGS. 2, 4, and 5, in order to significantly reduce or prevent the occurrence of cracks in the length-direction first and second outer layer sections 7 b 1 and 7 b 2, among the plurality of inner electrode layers 4, the first and second extension portions 4 c 1 and 4 c 2 included in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 are curved in the thickness direction T. Typically, all of the first and second extension portions 4 c 1 and 4 c 2 of the inner electrode layers 4 positioned toward the first principal surface 2 a 1 are curved toward the second principal surface 2 a 2, while all of the first and second extension portions 4 c 1 and 4 c 2 of the inner electrode layers 4 positioned toward the second principal surface 2 a 2 are curved toward the first principal surface 2 a 1.

With this configuration, compared with a case in which the first and second extension portions 4 c 1 and 4 c 2 are formed in a flat shape, that is, they are not curved in the thickness direction T, at the boundary between a ceramic dielectric layer 3 and an inner electrode layer 4, the resistance to the occurrence of interlayer delamination caused by a shear stress which would occur between a ceramic dielectric layer 3 and an inner electrode layer 4 is greatly increased. As a result, the occurrence of cracks is significantly reduced or prevented.

As discussed above, as in the first preferred embodiment, if the dimension t2 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is greater than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T, cracks are more likely to occur around the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2 rather than around the boundary between the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1. Accordingly, in order to more effectively reduce or prevent the occurrence of cracks in the length direction L, the multilayer ceramic capacitor 1A of the first preferred embodiment is configured in the following manner.

As shown in FIGS. 2 and 4, among the plurality of conductive layers connected to either one of the first and second outer electrodes 5 a and 5 b, the first extension portion 4 c 1 of the first outermost layer 4 a positioned closest to the first principal surface 2 a 1 is curved toward the second principal surface 2 a 2. As shown in FIGS. 2 and 5, among the plurality of conductive layers connected to either one of the first and second outer electrodes 5 a and 5 b, the second extension portion 4 c 2 of the second outermost layer 4 b positioned closest to the second principal surface 2 a 2 is curved toward the first principal surface 2 a 1.

As shown in FIGS. 2, 4, and 5, an amount C2 by which the second extension portion 4 c 2 of the second outermost layer 4 b is curved (hereinafter will be referred to as the curving amount C2 of the second extension portion 4 c 2) is greater than an amount C1 by which the first extension portion 4 c 1 of the first outermost layer 4 a is curved (hereinafter will be referred to as the curving amount C1 of the first extension portion 4 c 1) (C2>C1). The curving amount C1 refers to the distance in the thickness direction T between a portion of the main front surface of the first outermost layer 4 a positioned closer to the first principal surface 2 a 1 and included in the multilayer unit 10 and a portion of the main front surface of the first outermost layer 4 a connected to the first outer electrode 5 a, while the curving amount C2 refers to the distance in the thickness direction T between a portion of the main back surface of the second outermost layer 4 b positioned closer to the second principal surface 2 a 2 and included in the multilayer unit 10 and a portion of the main back surface of the second outermost layer 4 b connected to the second outer electrode 5 b.

With this configuration, it is possible to more reliably reduce or prevent the occurrence of cracks around the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2 in which the occurrence of cracks is more likely to occur.

In this case, as shown in FIG. 5, the curving amount C2 of the second extension portion 4 c 2 of the second outermost layer 4 b is preferably greater than a thickness x2 of a portion of a ceramic dielectric layer 3 disposed adjacent to the second outermost layer 4 b and included in the multilayer unit 10. With this configuration, it is possible to even more reliably reduce or prevent the occurrence of cracks around the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2.

Meanwhile, as a result of conducting an extensive study, the present inventors have discovered that the occurrence of cracks caused by an internal stress produced by the difference in the coefficients of thermal shrinkage between ceramic dielectric layers and conductive layers is capable of being significantly reduced or prevented by providing a specific configuration of the multilayer unit in the width direction, and have discovered that the following configuration of the multilayer unit in the width direction is effective.

As shown in FIG. 3, in order to significantly reduce or prevent the occurrence of the above-described cracks, the widthwise dimension of the multilayer unit 10 positioned toward the thickness-direction second outer layer section 6 b 2 is preferably set to be smaller, by a certain degree, than the widthwise dimension of the multilayer unit 10 positioned at the central portion in the thickness direction T. Typically, among the plurality of inner electrode layers 4 stacked on each other in the thickness direction T, the widthwise dimension of inner electrode layers 4 positioned toward the thickness-direction second outer layer section 6 b 2 gradually decreases as the inner electrode layers 4 are closer to the second principal surface 2 a 2.

With this configuration, it is possible to relax an internal stress which is produced by the difference in the coefficients of thermal shrinkage between ceramic dielectric layers and conductive layers and which acts on the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, thus making it possible to effectively reduce or prevent the occurrence of cracks in this boundary.

FIG. 6 illustrates the dimensional relationships among specific inner electrode layers in a predetermined cross section of the body 2 of the multilayer ceramic capacitor 1A of the first preferred embodiment of the present invention. FIGS. 7A and 7B illustrate the areal relationships among the specific inner electrode layers in this predetermined cross section.

As shown in FIGS. 3, 6, 7A, and 7B, in order to significantly reduce or prevent the occurrence of cracks, the multilayer ceramic capacitor 1A of the first preferred embodiment is configured in the following manner. Among the plurality of inner electrode layers 4 stacked on each other in the thickness direction T, the widthwise dimension of inner electrode layers 4 positioned toward the thickness-direction second outer layer section 6 b 2 gradually decreases as the inner electrode layers 4 are closer to the second principal surface 2 a 2. Accordingly, in the cross sections shown in FIGS. 3, 6, 7A, and 7B, the multilayer unit 10 is configured such that a rectangle and a trapezoid are connected to each other (one side of the rectangle and the longer side of a pair of parallel sides of the trapezoid join each other).

A brief description will be given below of the characteristics of the configuration of the multilayer unit 10 which is particularly effective to significantly reduce or prevent the occurrence of cracks that are most likely to occur in the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2 along the width direction W.

In FIG. 6, among the plurality of inner electrode layers 4, a dimension we2 of the second conductive layer 4 b in the width direction W disposed closest to the second principal surface 2 a 2 is smaller than a dimension we3 of a central inner electrode layer 4 c, which defines and serves as a third conductive layer, positioned closest to the thickness-direction central portion of the multilayer unit 10 (we2<we3). With this configuration, at least in the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, an internal stress produced by the difference in the coefficients of thermal shrinkage between ceramic dielectric layers and inner electrode layers is relaxed.

In this case, it is preferable that the dimension we2 of the second conductive layer 4 b is about 0.5 to about 0.95 times as large as the dimension we3 of the central inner electrode layer 4 c (0.5≦we2/we3≦0.95), for example. If the dimension we2 of the second conductive layer 4 b is less than about 0.5 times as large as the dimension we3 of the central inner electrode layer 4 c, the electrostatic capacitance is decreased in relation to the size of the multilayer ceramic capacitor 1A. Thus, it is difficult to increase the electrostatic capacitance and to decrease the size of the multilayer ceramic capacitor 1A at the same time. If the dimension we2 of the second conductive layer 4 b is more than about 0.95 times as large as the dimension we3 of the central inner electrode layer 4 c, the above-described effect of significantly reducing or preventing the occurrence of cracks is not sufficiently exhibited.

If an increase in the capacity of the multilayer ceramic capacitor 1A is also taken into consideration, in addition to the above-described characteristics of the configuration of the multilayer unit 10, the following condition is preferably satisfied. In a certain cross section passing through the multilayer unit 10 and parallel with both of the width direction W and the thickness direction T, areas S1 and S2, which will be defined as follows, preferably satisfy the relationship expressed by 0.75≦S2/S≦0.95, for example.

In the cross section of the body 2 shown in FIG. 7A, the area S1 is an area of a rectangular or substantially rectangular region indicated by the hatched portion in FIG. 7A, and more specifically, an area surrounded by a first virtual line VL1 passing through the second conductive layer 2 b (more precisely, passing through the main back surface of the second conductive layer 4 b closer to the second principal surface 2 a 2), a second virtual line VL2 passing through the above-described largest-width inner electrode layer 4 d (more precisely, passing through the main front surface of the largest-width inner electrode layer 4 d closer to the first principal surface 2 a 1), a third virtual line VL3 passing through one widthwise end of the largest-width inner electrode layer 4 d and being parallel or substantially parallel with the thickness direction T, and a fourth virtual line VL4 passing through the other widthwise end of the largest-width inner electrode layer 4 d and being parallel or substantially parallel with the thickness direction T.

In FIG. 7B, the area S2 is an area of a portion of the multilayer unit 10 from the largest-width inner electrode layer 4 d to the second conductive layer 4 b. More specifically, the area S2 is an area of a trapezoidal or substantially trapezoidal region having step-shaped portions at both ends, indicated by the hatched portion in FIG. 7B. The trapezoidal or substantially trapezoidal region is a portion defining the above-described capacitor elements in this region.

If the condition that the value defined by S2/S1 concerning the areas S1 and S2 (that is, the ratio of the area S2 to the area S1) is about 0.75 to about 0.95 (that is, 0.75≦S2/S1≦0.95) is satisfied, the electrostatic capacitance is not considerably reduced in relation to the size of the multilayer ceramic capacitor 1A. It is thus possible to increase the electrostatic capacitance and to decrease the size of the multilayer ceramic capacitor 1A at the same time.

In order to even more effectively significantly reduce or prevent the occurrence of cracks caused by an internal stress, in addition to the above-described conditions, the conditions which will be discussed below are preferably satisfied. Note that such conditions are based on the following knowledge. The occurrence of cracks produced within the body 2 of the multilayer ceramic capacitor 1A is capable of being reduced or prevented by increasing an adhesion force of a ceramic dielectric material in the width-direction first and second outer layer sections and that in the length-direction first and second outer layer sections and/or by increasing an adhesion force between the ceramic dielectric material and a conductor material in the length-direction first and second outer layer sections. More specifically, the occurrence of cracks is capable of being reduced or prevented, in a step of fixing a set of material sheets with pressure (St5) in a manufacturing flow (see FIG. 8) of multilayer ceramic capacitors in the first preferred embodiment, by applying a sufficient pressure force to portions which will define the width-direction first and second outer layer sections 8 b 1 and 8 b 2 and the length-direction first and second outer layer sections 7 b 1 and 7 b 2.

As shown in FIG. 3, both of dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W are preferably greater than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T (w1>t1 and w2>t1).

In the multilayer ceramic capacitor 1A of the first preferred embodiment, the dimension of the multilayer unit 10 in the width direction W preferably is not uniform in the thickness direction T, as discussed above. Accordingly, the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W are also non-uniform in the thickness direction T. Thus, the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2 in the width direction W are respectively determined by the dimensions of the width-direction first and second outer layer sections 8 b 1 and 8 b 2 next to the first conductive layer 4 a and/or the second conductive layer 4 b. In other words, the dimension w1 of the width-direction first outer layer sections 8 b 1 preferably correspond to a distance between the multilayer unit 10 and the first side surface 2 c 1 on a widthwise line through the first conductive layer 4 a in the width direction. The dimension w2 of the width-direction second outer layer sections 8 b 2 preferably corresponds to a distance between the multilayer unit 10 and the second side surface 2 c 2 in the width direction. When the dimensions w1, w2, t1 cannot be determined precisely, a minimum value of the dimensions can be selected.

With this configuration, the adhesion force of the ceramic dielectric material in the width-direction first and second outer layer sections 8 b 1 and 8 b 2 significantly increases, thus effectively significantly reducing or preventing the occurrence of cracks caused by an internal stress in these sections.

More preferably, both of the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W are more than about 1.3 times as large as the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T (w1/t1>1.3 and w2/t1>1.3), for example. With this configuration, it is possible to more reliably reduce or prevent the occurrence of cracks caused by an internal stress in the width-direction first and second outer layer sections 8 b 1 and 8 b 2.

As shown in FIG. 2, both of dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2, respectively, in the length direction L are preferably greater than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T (11>t1 and 12>t1). With this configuration, the adhesion force of the ceramic dielectric material and the adhesion force between the ceramic dielectric material and the conductor material in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 significantly increases, thus effectively reducing or preventing the occurrence of cracks caused by an internal stress in these sections. The dimension 11 of the length-direction first outer layer sections 7 b 1 preferably correspond to a distance between the multilayer unit 10 and the first end surface 2 b 1 in the length direction. The dimension 12 of the length-direction second outer layer sections 7 b 2 preferably correspond to a distance between the multilayer unit 10 and the second end surface 2 b 2 in the length direction. When the dimensions l1, l2, t1 cannot be determined precisely, a minimum value of the dimensions can be selected as the dimensions l1, l2, t1. More preferably, both of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2, respectively, in the length direction L are more than about 1.5 times as large as the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T (l1/t1>1.5 and l2/t1>1.5), for example. With this configuration, it is possible to more reliably reduce or prevent the occurrence of cracks caused by an internal stress in the length-direction first and second outer layer sections 7 b 1 and 7 b 2.

In FIGS. 2 and 3, the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T is preferably about 40 μm or smaller, for example. If the dimension t1 is large, the difference in the coefficients of thermal shrinkage between the thickness-direction inner layer section 6 a including the multilayer unit 10 and the thickness-direction first outer layer section 6 b 1 without the multilayer unit 10 becomes more noticeable. This may significantly increase a shear stress caused by the difference in the coefficients of thermal shrinkage, thus increasing the possibility that cracks will occur at the boundary between the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1. With the dimension t1 having a thickness of about 40 μm or smaller, for example, the difference in the coefficients of thermal shrinkage is significantly reduced or minimized, thereby effectively reducing or preventing the occurrence of cracks at this boundary.

As stated above, the dimension t2 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T preferably is greater than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T. While considering a tradeoff relationship in which by increasing the dimension t2, the occurrence of cracks due to an external stress is significantly reduced or prevented, but on the other hand, the occurrence of cracks due to an internal stress is increased, the dimension t2 is reduced to be as small as possible, thus significantly reducing or preventing the occurrence of cracks at the boundary between the thickness-direction inner layer section 6 a including the multilayer unit 10 and the thickness-direction second outer layer section 6 b 2 without the multilayer unit 10.

In FIG. 3, both of the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2 in the width direction W are preferably about 52 μm or greater, for example. With this configuration, the adhesion force of the ceramic dielectric material in the width-direction first and second outer layer sections 8 b 1 and 8 b 2 significantly increases, thus effectively significantly reducing or preventing the occurrence of cracks due to an internal stress in these sections.

In FIG. 2, both of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2 in the length direction L are preferably about 60 μm or greater, for example. With this configuration, the adhesion force of the ceramic dielectric material and the adhesion force between the ceramic dielectric material and the conductor material in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 significantly increase, thus effectively reducing or preventing the occurrence of cracks due to an internal stress in these sections.

In FIGS. 2 and 3, the thickness x1 of each of the plurality of inner electrode layers 4 contained in the multilayer unit 10 is preferably about 0.8 times or less as large as the thickness x2 of each of the plurality of ceramic dielectric layers 3 contained in the multilayer unit 10 (x1/x2≦0.8), for example.

With this configuration, after the step of stacking material sheets (St4) in the manufacturing flow (see FIG. 8) of multilayer ceramic capacitors in the first preferred embodiment, the difference between the total thickness of ceramic bases 12 and conductor patterns 13 which will define the multilayer unit 10 and the total thickness of ceramic bases 12 which will define the length-direction first and second outer layer sections 7 b 1 and 7 b 2 and the width-direction first and second outer layer sections 8 b 1 and 8 b 2 and conductor patterns 13 which will define the length-direction first and second outer layer sections 7 b 1 and 7 b 2 is reduced (see FIGS. 10A through 11B).

Thus, in the step of fixing a set of material sheets with pressure (St5) in the manufacturing flow (see FIG. 8), a sufficient pressure force is applied to portions which will define the length-direction first and second outer layer sections 7 b 1 and 7 b 2 and the width-direction first and second outer layer sections 8 b 1 and 8 b 2. As a result, the occurrence of cracks in these portions caused by an internal stress is effectively significantly reduced or prevented.

In FIGS. 2 and 3, each of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2, respectively, in the length direction L is preferably greater than the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W (l1>w1, l1>w2, l2>w1, l2>w2).

As stated above, the length-direction first and second outer layer sections 7 b 1 and 7 b 2 are respectively constituted by ceramic dielectric layers 3 and the inner electrode layers 4 which will define the first and second extension portions 4 c 1 and 4 c 2. On the other hand, the width-direction first and second outer layer sections 8 b 1 and 8 b 2 are constituted only by ceramic dielectric layers 3 and do not include any inner electrode layer 4. Thus, interlayer delamination is likely to occur in the boundary between the first and second extension portions 4 c 1 and 4 c 2 and adjacent ceramic dielectric layers 3 in the length-direction first and second outer layer sections 7 b 1 and 7 b 2, as discussed above.

Concerning this point, from the viewpoint of significantly reducing or preventing the occurrence of interlayer delamination in the length-direction first and second outer layer sections 7 b 1 and 7 b 2, it is preferable that each of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2 be greater than the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, which are set so that the occurrence of cracks in the width-direction first and second outer layer sections 8 b 1 and 8 b 2 is significantly reduced or prevented.

With the above-described configuration, not only the occurrence of cracks in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 and the width-direction first and second outer layer sections 8 b 1 and 8 b 2 caused by an internal stress can be significantly reduced or prevented, but also the occurrence of interlayer delamination in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 caused by an internal stress can be significantly reduced or prevented.

More preferably, each of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2 in the length direction L is more than about 1.15 times as large as the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2 in the width direction W (l1/w1>1.15, l1/w2>1.15, l2/w1>1.15, l2/w2>1.15), for example. With this configuration, it is possible to more reliably reduce or prevent the occurrence of interlayer delamination in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 caused by an internal stress.

FIG. 8 is a flowchart illustrating a non-limiting example of a manufacturing flow for the multilayer ceramic capacitor 1A shown in FIG. 1. The manufacturing flow for the multilayer ceramic capacitor 1A will be discussed below with reference to FIG. 8. In this manufacturing flow, a plurality of multilayer ceramic capacitors 1A are mass-produced together in the following manner. A material which will form a plurality of multilayer ceramic capacitors 1A is processed together until a halfway point through a manufacturing process so as to fabricate a mother block. Then, the mother block is divided into individual chips, and the individual chips are then processed.

The manufacturing process will be discussed below more specifically. In step St1, ceramic slurry is prepared first. More specifically, a ceramic powder, a binder, and a solvent are mixed at a predetermined mixing ratio so as to form ceramic slurry.

Then, in step St2, ceramic green sheets are formed. More specifically, the ceramic slurry is formed into a sheet-shaped shape on a carrier film by using a die coater, a gravure coater, or a micro gravure coater, thereby forming ceramic green sheets.

Then, in step St3, material sheets are formed. More specifically, a conductor paste is printed on each ceramic green sheet by using screen printing or gravure printing such that a predetermined conductor pattern is formed on the ceramic green sheet. As a result, a material sheet having a predetermined conductor pattern on a ceramic green sheet is formed.

Material sheets formed in step St3 will be discussed below in details. FIG. 9 is an exploded perspective view illustrating the multilayer structure of a set of base sheets 11, which will form the body 2 of the multilayer ceramic capacitor 1A shown in FIG. 1.

As shown in FIG. 9, the body 2 is fabricated by using the set of base sheets 11 constituted by a plurality of base sheets 11A, 11B1, and 11B2 which are configured differently. More specifically, the body 2 is fabricated by stacking the plurality of base sheets 11A, 11B1, and 11B2 in a predetermined order and by then fixing them with pressure and firing them.

The base sheet 11A is constituted only by a ceramic base 12 on which no conductor pattern is formed. The base sheet 11A will be used as a ceramic dielectric layer 3 which forms the thickness-direction first or second outer layer section 6 b 1 or 6 b 2 after the body 2 is fired.

The base sheets 11B1 and 11B2 are each constituted by a ceramic base 12 on which a conductor pattern 13 having a predetermined shape is formed. The conductor patterns 13 of the base sheets 11B1 and 11B2 will be used as inner electrode layers 4 after the body 2 is fired. The ceramic bases 12 of the base sheets 11B1 and 11B2 will be used as ceramic dielectric layers 3, most of which will form the thickness-direction inner layer section 6 a.

The layout of a material sheet formed in step St3 is as follows. By using the base sheet 11B1 or 11B2 shown in FIG. 9 as a unit, a plurality of base sheets having the same shape as that of the base sheet 11B1 or 11B2 which is determined as a unit are two-dimensionally arranged in a matrix.

As material sheets, not only material sheets having the above-described conductor patterns, but also ceramic green sheets which are formed without being subjected to step St3 are also prepared.

Then, referring back to FIG. 8, in step St4, the material sheets are stacked. More specifically, by stacking the plurality of material sheets according to a predetermined rule, the above-described units (base sheets 11B1 and 11B2) are disposed within the stacked material sheets in the stacking direction so as to obtain the multilayer structure shown in FIG. 9.

Then, in step St5, the set of stacked material sheets is fixed with pressure. More specifically, pressure is applied to the set of material sheets in the stacking direction by using, for example, isostatic pressing, thereby fixing the set of material sheets.

FIGS. 10A through 11B are schematic sectional views illustrating a step of fixing a set of material sheets 20 with pressure in step St5 of FIG. 8. FIGS. 10A and 10B are sectional views along the length direction L of the multilayer ceramic capacitor 1A to be manufactured, and FIGS. 11A and 11B are sectional views along the width direction W thereof. FIGS. 10A and 11A illustrate the state of the set of material sheets 20 which have not yet been fixed with pressure, while FIGS. 10B and 11B illustrate the state of the set of material sheets 20 which have been fixed with pressure.

As shown in FIGS. 10A through 11B, in step St5, the set of material sheets 20 which are stacked according to the predetermined rule are sandwiched between a pair of pressure plates 50 in the stacking direction, and isostatic pressure is applied to the pressure plates 50, thereby fixing the set of material sheets 20.

As shown in FIG. 10A, regions X in which many conductor patterns 13 are disposed and regions Y in which a relatively small number of conductor patterns 13 are disposed are alternately arranged in the length direction L of the set of material sheets 20. The region X will form the length-direction inner layer section 7 a of the multilayer ceramic capacitor 1A, while the region Y will form the length-direction first or second outer layer section 7 b 1 or 7 b 2 of the multilayer ceramic capacitor 1A.

As shown in FIG. 11A, regions X in which many conductor patterns 13 are disposed and regions Z in which no conductor pattern 13 is disposed are alternately arranged in the width direction W of the set of material sheets 20. The region X will form the width-direction inner layer section 8 a of the multilayer ceramic capacitor 1A, while the region Z will form the width-direction first or second outer layer section 8 b 1 or 8 b 2 of the multilayer ceramic capacitor 1A.

A sheet-shaped elastic member 60 is interposed between each of the pressure plates 50 and the set of material sheets 20. The sheet-shaped elastic members 60 are used to adjust a pressure force to be applied to the individual regions of the set of material sheets 20 through the pair of pressure plates 50. The sheet-shaped elastic members 60 are made of a resin, for example, rubber.

Since the ceramic bases 12 are made of a ceramic dielectric material, they are relatively soft and are easy to press. In contrast, since the conductor patterns 13 are made of a conductor material, they are relatively hard and are difficult to press. In the regions X, many conductor patterns 13 are densely disposed, and on the other hand, in the regions Y, a smaller number of conductor patterns 13 are disposed than in the regions X, and in the regions Z, no conductor pattern 13 is disposed. Accordingly, it is relatively difficult to press the regions X but it is relatively easy to apply a pressing force to the regions X, while it is relatively easy to press the regions Y and Z but it is relatively difficult to apply a pressing force to the regions Y and Z.

Thus, as discussed above, a sheet-shaped elastic member 60 is interposed between each of the pressure plates 50 and the set of material sheets 20. The set of material sheets 20 are fixed with pressure by using the pressure plates 50 via the sheet-shaped elastic members 60, and then, the sheet-shaped elastic members 60 are elastically deformed so as to adjust the pressure force to be applied to the individual regions of the set of material sheets 20. Accordingly, not only in the regions X in which many conductor patterns 13 are densely disposed, but also in the regions Y in which a smaller number of conductor patterns 13 are disposed than in the regions X and in the regions Z in which no conductor pattern 13 is disposed can be pressed with a sufficient pressing force. As a result, the conductor patterns 13 which will form the first and second extension portions 4 c 1 and 4 c 2 can be curved, as shown in FIGS. 2, 4, and 5.

In order to manufacture the multilayer ceramic capacitor 1A of the first preferred embodiment in which the curving amount C2 of the second extension portion 4 c 2 of the second outermost layer 4 b is greater than the curving amount C1 of the first extension portion 4 c 1 of the first outermost layer 4 a, the thickness of one sheet-shaped elastic member 60 interposed between one pressure plate 50 and the set of material sheets 20 may be changed from that of the other sheet-shaped elastic member 60 interposed between the other pressure plate 50 and the set of material sheets 20, as shown in FIGS. 10A through 11B.

More specifically, as shown in FIGS. 10A through 11B, the thickness of the sheet-shaped elastic member 60 disposed closer to the first outermost layer 4 a is relatively small, while the thickness of the sheet-shaped elastic member 60 disposed closer to the second outermost layer 4 b is relatively large. With this arrangement, it is possible to adjust the pressing force to be applied to the regions Y in the stacking direction, thereby making it possible to obtain the multilayer ceramic capacitor 1A configured as described above.

For obtaining the multilayer ceramic capacitor 1A configured as described above, the step of stacking the material sheets in step St4 is preferably performed in the following manner. Stacking of material sheets is started from a material sheet which will form the first principal surface 2 a 1, and every time one material sheet is stacked on another material sheet, the stacked material sheets are pressed. Then, the above-described fixing step in St5 is performed. By using this technique, in accordance with the relationship between the accumulation of pressing force repeatedly applied to the material sheets as a result of pressing them and the presence or the absence of the conductor patterns 13 or the density of the conductor patterns 13 in the regions X, Y, and Z, it is more likely to obtain the multilayer ceramic capacitor 1A configured as described above. If this technique is used, in the fixing step St5, the provision of only a sheet-shaped elastic member 60 closer to the second outermost layer 4 b is sufficient, and the provision of a sheet-shaped elastic member 60 closer to the first outermost layer 4 a may be omitted.

In order to manufacture the multilayer ceramic capacitor 1A of the first preferred embodiment in which the widthwise dimension of the multilayer unit 10 is not uniform in the thickness direction T, material sheets including conductor patterns 13 having non-uniform widthwise dimensions are prepared, and then, they are stacked in a predetermined order, as shown in FIG. 11A.

Alternatively, material sheets including conductor patterns 13 having uniform widthwise dimensions may be used. In this case, however, the conductor patterns 13 have different thicknesses, and when they are pressed, they extend to different widthwise dimensions. In this manner, it is possible to manufacture the multilayer ceramic capacitor 1A in which the widthwise dimension of the multilayer unit 10 is not uniform in the thickness direction T.

Alternatively, material sheets including conductor patterns 13 having the same configuration and the same dimensions (that is, having the uniform widthwise dimension and uniform thickness dimension) may be used. In this case, however, the pressing force applied in isostatic pressing in step St5 is adjusted or pressing of material sheets when stacking the material sheets in step St4 is suitably performed. In this manner, it is possible to manufacture the multilayer ceramic capacitor 1A in which the widthwise dimension of the multilayer unit 10 is not uniform in the thickness direction T.

By fixing the set of material sheets 20 with pressure as described above, a mother block 30 shown in FIGS. 10B and 11B is fabricated.

Then, in step St6, the mother block 30 is divided. More specifically, the mother block 30 is divided in a matrix form by push-cutting or dicing, thereby cutting out the above-described individual chips. Each of the chips cut out from the mother block 30 has a multilayer structure, such as that shown in FIG. 9.

Then, in step St7, the chips are fired. More specifically, the chips are heated to a predetermined temperature, thereby performing sintering on the ceramic dielectric material and the conductor material.

Then, in step St8, the chips are barrel-polished. More specifically, the chips subjected to firing are sealed within a small box called a barrel, together with media balls having a higher hardness than the ceramic dielectric material. Then, by rotating the barrel, the chips can be polished. By performing this barrel-polishing, the outer surfaces (in particular, corners) of the chips are curved and rounded. As a result, the above-described body 2 is formed.

Then, in step St9, outer electrodes are formed. More specifically, a conductor paste is applied to end portions including the first and second end surfaces 2 b 1 and 2 b 2 of the body 2 so as to form a metal film, and then, sintering processing is performed on the metal film. Then, the metal film is sequentially Ni-plated and Sn-plated. As a result, the first and second outer electrodes 5 a and 5 b are formed on the outer surfaces of the body 2.

After the above-described series of steps, the multilayer ceramic capacitor 1A configured as shown in FIGS. 1 through 5 is manufactured.

FIG. 12 is a sectional view illustrating a multilayer ceramic capacitor mount body 100 of the first preferred embodiment. The multilayer ceramic capacitor mount body 100 will be described below with reference to FIG. 12.

As shown in FIG. 12, the multilayer ceramic capacitor mount body 100 of the first preferred embodiment includes the above-described multilayer ceramic capacitor 1A and a wiring board 101, which defines and serves as a mounting member on which the multilayer ceramic capacitor 1A is mounted. The multilayer ceramic capacitor 1A is mounted on the wiring board 101 such that its second principal surface 2 a 2 faces the wiring board 101. As the mounting board, a member other than the wiring board 101 may be used.

The configuration of the multilayer ceramic capacitor mount body 100 will be discussed more specifically. A pair of lands 102 is disposed on the surface of the wiring board 101 such that the lands 102 are spaced apart from each other. The first and second outer electrodes 5 a and 5 b of the multilayer ceramic capacitor 1A are disposed on the lands 102 such that the first outer electrode 5 a faces one land 102 and the second outer electrode 5 b faces the other land 102. Solder 103, which is a bonding medium, is disposed each of between the first outer electrode 5 a and one land 102 and between the second outer electrode 5 b and the other land 102, thus bonding the first and second outer electrodes 5 a and 5 b to the respective lands 102. As the bonding medium, a medium other than the solder 103 may be used.

A dimension WL of the pair of lands 102 in the width direction W is preferably smaller than the dimension W0 of the body 2 in the width direction W. With this configuration, the first and second outer electrodes 5 a and 5 b are subjected to a compressive stress applied from the solder 103 along the width direction W when the solder 103 is solidified. This compressive stress also acts on a boundary portion between the multilayer unit 10 and the thickness-direction second outer layer section 6 b 2. Accordingly, with the above-described configuration, the stress acting on this boundary portion is relaxed, thus significantly reducing or preventing the occurrence of cracks in this boundary portion.

Additionally, the dimension WL of the pair of lands 102 in the width direction W is preferably smaller than the dimension of the second conductive layer 4 b (the conductive layer positioned closest to the second principal surface 2 a 2) among the plurality of conductive layers included in the multilayer unit 10, though the multilayer ceramic capacitor mount body 100 shown in FIG. 12 is not configured in such a manner. With this configuration, when the solder 103 is solidified, the compressive stress acting on the boundary portion between the multilayer unit 10 and the thickness-direction second outer layer section 6 b 2 is further enhanced. This further relaxes the stress acting on this boundary portion, thus significantly reducing or preventing the occurrence of cracks in this boundary portion more reliably.

FIG. 13 is a plan view illustrating a multilayer ceramic capacitor array 200 of the first preferred embodiment. FIG. 14 is a schematic sectional view taken along line XIV-XIV of FIG. 13. The multilayer ceramic capacitor array 200 of the first preferred embodiment will be described below with reference to FIGS. 13 and 14.

As shown in FIGS. 13 and 14, the multilayer ceramic capacitor array 200 of the first preferred embodiment includes a plurality of multilayer ceramic capacitors 1A discussed above and a package 201 to package the plurality of multilayer ceramic capacitors 1A together therein. The package 201 includes an elongated carrier tape 202 and a cover tape 203. The carrier tape 202 includes a plurality of recessed portions 202 a disposed apart from each other and storing the plurality of multilayer ceramic capacitors 1A therein. The cover tape 203 is attached to the carrier tape 202 such that it covers the plurality of recessed portions 202 a. The plurality of multilayer ceramic capacitors 1A are stored in the respective recessed portions 202 a such that their second principal surfaces 2 a 2 face bottom portions 202 b of the respective recessed portions 202 a.

The plurality of multilayer ceramic capacitors 1A contained in the multilayer ceramic capacitor array 200 are extracted from the package 201 one by one and are mounted on the above-described wiring board 101. More specifically, in the state in which the cover tape 203 is removed from the carrier tape 202, the multilayer ceramic capacitors 1A are sucked and held at the side from their first principal surfaces 2 a 1 by a suction head, such as a chip mounter, so as to be removed from the carrier tape 202 and mounted on the wiring board 101.

As stated above, the multilayer ceramic capacitors 1A are stored in the respective recessed portions 202 a such that their second principal surfaces 2 a 2 face the bottom portions 202 b of the respective recessed portions 202 a. With this arrangement, a mounting operation using a suction head, such as a chip mounter, can be performed smoothly. Thus, by forming the multilayer ceramic capacitor array 200 of the first preferred embodiment as described above, it is possible to easily manufacture the above-described multilayer ceramic capacitor mount body 100 of the first preferred embodiment.

Second Preferred Embodiment

FIG. 15 is a schematic perspective view illustrating a multilayer ceramic capacitor 1B according to a second preferred embodiment of the present invention. FIGS. 16 and 17 are schematic sectional views taken along lines XVI-XVI and XVII-XVII, respectively, of FIG. 15. The configuration of the multilayer ceramic capacitor 1B of the second preferred embodiment will be described below with reference to FIGS. 15 through 17.

As shown in FIGS. 15 through 17, the multilayer ceramic capacitor 1B of the second preferred embodiment is different from the multilayer ceramic capacitor 1A of the first preferred embodiment in the configuration of the thickness-direction second outer layer section 6 b 2, for example. More specifically, the thickness-direction second outer layer section 6 b 2 of the multilayer ceramic capacitor 1B includes an inner portion 6 b 21 disposed adjacent to the thickness-direction inner layer section 6 a and an outer portion 6 b 22 which is disposed adjacent to the inner portion 6 b 21 and which defines the second principal surface 2 a 2.

The inner portion 6 b 21 is constituted by a ceramic dielectric layer 3 made of a ceramic dielectric material, which preferably is the same type (that is, having the same composition) as that of the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1. The outer layer 6 b 22 is constituted by a ceramic dielectric layer 9 made of a ceramic dielectric material, which is a different type (that is, having a different composition) from that of the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1.

The ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 and the ceramic dielectric layer 9 defining the outer portion 6 b 22 contain a perovskite compound expressed by ABO₃ (“A” contains Ba and “B” contains Ti) as a principal component. A typical example of a perovskite compound expressed by ABO₃ is barium titanate (BaTiO₃).

The ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 and the ceramic dielectric layer 9 defining the outer portion 6 b 22 contain Si as a secondary component. Si is contained in the ceramic dielectric layers 3 and 9 by adding a Si compound, such as glass or SiO₂, to a perovskite compound expressed by ABO₃. Another compound, such as a Mn compound, an Mg compound, a Co compound, a Ni compound, or a rare earth compound, may be added to a perovskite compound expressed by ABO₃.

The composition ratio of Si to Ti contained in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is higher than that in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21. The composition ratio is typically represented by a molar ratio. The molar ratio of Si to Ti contained in the ceramic dielectric layer 3 and that in the ceramic dielectric layer 9 may be measured by using a wavelength-dispersive X-ray spectrometer (WDX), for example.

The molar ratio of Si to Ti contained in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is preferably about 0.013 mol to about 0.030 mol, for example. If the molar ratio of Si to Ti contained in the ceramic dielectric layer 9 is lower than about 0.013 mol or higher than about 0.030 mol, the reliability of the outer portion 6 b 22 may be decreased.

The molar ratio of Si to Ti contained in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is preferably higher than that in the ceramic dielectric layer 3 defining the inner portion 6 b 21 by about 0.004 mol or higher, and more preferably by about 0.008 mol or higher, for example.

A boundary portion P1 of the outer portion 6 b 22 with the inner portion 6 b 21 has a larger Si content than the thickness-direction central portion of the outer portion 6 b 22. A surface layer portion P2 of the outer portion 6 b 22 close to the second principal surface 2 a 2 also has a higher Si content than the thickness-direction central portion of the outer portion 6 b 22. A determination as to whether or not the boundary portion P1 and the surface layer portion P2 of the outer portion 6 b 22 have a high Si content ratio may be made by element mapping created by using a field emission wavelength-dispersive X-ray spectrometer (FE-WDX), for example.

The multilayer ceramic capacitor 1B of the second preferred embodiment, as well as the multilayer ceramic capacitor 1A of the first preferred embodiment, includes the first and second extension portions 4 c 1 and 4 c 2 and the multilayer unit 10 preferably configured similar to those of the first preferred embodiment, as shown in FIGS. 16 and 17. Thus, advantages similar to those discussed in the first preferred embodiment can also be obtained.

Additionally, in the multilayer ceramic capacitor 1B of the second preferred embodiment, as stated above, the molar ratio of Si to Ti contained in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is higher than that in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21. That is, the outer portion 6 b 22 contains a greater amount of Si than the inner portion 6 b 21. The coefficient of thermal shrinkage of a ceramic dielectric layer having a higher Si content ratio is greater than that of a ceramic dielectric layer having a lower Si content ratio. Accordingly, the coefficient of thermal shrinkage of the outer portion 6 b 22 is greater than that of the inner portion 6 b 21. Thus, the coefficient of thermal shrinkage of the outer portion 6 b 22 is closer to that of the inner electrode layers 4 included in the thickness-direction inner layer section 6 a.

Thus, in the multilayer ceramic capacitor 1B, it is possible to relax an internal stress which is caused by the difference in the coefficients of thermal shrinkage between the ceramic dielectric layers 3 and the inner electrode layers 4 and which acts on the boundary portion between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, thus effectively reducing or preventing the occurrence of cracks in this boundary portion.

If the molar ratio of Si to Ti contained in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is higher than that in the ceramic dielectric layer 3 defining the inner portion 6 b 21 by about 0.004 mol or higher, the occurrence of cracks in this boundary portion is reduced or prevented more effectively. If the above-described molar ratio is higher by about 0.008 mol or higher, the occurrence of cracks in this boundary portion is reduced or prevented even more effectively.

As shown in FIG. 16, in the multilayer ceramic capacitor 1B of the second preferred embodiment, part of the outer portion 6 b 22 which corresponds to the length-direction first and second outer layer sections 7 b 1 and 7 b 2 protrudes toward the inner portion 6 b 21, thus defining curved-and-swelled portions 9 a. As shown in FIG. 17, part of the outer portion 6 b 22 which corresponds to the width-direction first and second outer layer sections 8 b 1 and 8 b 2 protrudes toward the inner portion 6 b 21, thus defining curved-and-swelled portions 9 b.

The curved-and-swelled portions 9 a and 9 b can be formed easily in the following manner. When a base sheet which will be used as the ceramic dielectric layer 9 defining the outer portion 6 b 22 is attached to and fixed with pressure to a mother block on which the inner portion 6 b 21 has already been formed, an elastic member is inserted between the pressure plate and the mother block having this base sheet attached thereto. By suitably adjusting the thickness and the material of the elastic member, the pressure force to be applied, the thickness of the base sheet to be attached, or the configuration of the outer surface of the mother block, the configurations of the curved-and-swelled portions 9 a and 9 b preferably are adjusted.

In the multilayer ceramic capacitor 1B configured as described above, since the interface between the outer portion 6 b 22 and the inner portion 6 b 21 has a non-planar shape, the adhesion force between the outer portion 6 b 22 and the inner portion 6 b 21 is increased, thus making it possible to prevent the occurrence of delamination between the outer portion 6 b 22 and the inner portion 6 b 21, compared with a case in which the interface between the outer portion 6 b 22 and the inner portion 6 b 21 has a planar shape. As a result, with this configuration, it is possible to provide a more reliable multilayer ceramic capacitor.

In the multilayer ceramic capacitor 1B of the second preferred embodiment, in order to even more effectively reduce or prevent the occurrence of cracks caused by an internal stress, the following conditions are preferably satisfied. Some of the following conditions have been established on the basis of evaluation results of first and second verification tests, which will be discussed later.

As shown in FIG. 17, both of dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W are preferably greater than a dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T (w1>t21 and w2>t21). With this configuration, the adhesion force of the ceramic dielectric material in the width-direction first and second outer layer sections 8 b 1 and 8 b 2 significantly increases, thus effectively reducing or preventing the occurrence of cracks caused by an internal stress in these sections.

More preferably, both of the dimensions w1 and w2 of the width-direction first and second outer layer sections 8 b 1 and 8 b 2, respectively, in the width direction W are more than about 1.3 times as large as the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T (w1/t21>1.3 and w2/t21>1.3), for example. With this configuration, it is possible to more reliably reduce or prevent the occurrence of cracks caused by an internal stress in the width-direction first and second outer layer sections 8 b 1 and 8 b 2.

As shown in FIG. 16, both of dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2, respectively, in the length direction L are preferably greater than the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T (l1>t21 and l2>t21). With this configuration, the adhesion force of the ceramic dielectric material and the adhesion force between the ceramic dielectric material and the conductor material in the length-direction first and second outer layer sections 7 b 1 and 7 b 2 significantly increase, thus effectively reducing or preventing the occurrence of cracks caused by an internal stress in these sections.

More preferably, both of the dimensions l1 and l2 of the length-direction first and second outer layer sections 7 b 1 and 7 b 2, respectively, in the length direction L are more than about 1.5 times as large as the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T (l1/t21>1.5 and l2/t21>1.5), for example. With this configuration, it is possible to more reliably reduce or prevent the occurrence of cracks caused by an internal stress in the length-direction first and second outer layer sections 7 b 1 and 7 b 2.

As shown in FIGS. 16 and 17, the dimension t22 of the outer portion 6 b 22 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is preferably equal to or greater than the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T. With this configuration, the above-described stress relaxing effect exhibited by the thermal shrinkage of the outer portion 6 b 22 is more likely to be produced at the boundary portion between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, thus effectively reducing or preventing the occurrence of cracks at this boundary portion.

In FIGS. 16 and 17, the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is preferably about 20 μm or greater, for example. With this configuration, the diffusion of Si contained in the outer portion 6 b 22 into the thickness-direction inner layer section 6 a is reduced or prevented. If the Si content ratio in the thickness-direction inner layer section 6 a is too high, the grain growth of ceramic particles in the ceramic dielectric layers 3 included in the thickness-direction inner layer section 6 a accelerates excessively in a step of firing the body 2, thus reducing the withstand voltage characteristics of the ceramic dielectric layers 3. As a result, the thickness-direction inner layer section 6 a is more likely to be short-circuited. However, with the above-described configuration, it is possible to significantly reduce or prevent the occurrence of the short-circuiting of the thickness-direction inner layer section 6 a by maintaining the withstand voltage characteristics of the ceramic dielectric layers 3 included in the thickness-direction inner layer section 6 a.

The dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T preferably is smaller than the dimension t1 of the thickness-direction first outer layer section 6 b 1 in the thickness direction T, for example. Even with this configuration, because of the provision of the outer portion 6 b 22 outside the inner portion 6 b 21, the entry of moisture into the thickness-direction inner layer section 6 a from the inner portion 6 b 21 and the outer portion 6 b 22 is significantly reduced or prevented. Thus, even if the dimension t21 of the inner portion 6 b 21 of the thickness-direction second outer layer section 6 b 2 is reduced to be sufficiently small, the reliability is not decreased.

In FIGS. 16 and 17, the dimension t22 of the outer portion 6 b 22 of the thickness-direction second outer layer section 6 b 2 in the thickness direction T is preferably about 30 μm or greater, for example. With this configuration, the above-described stress relaxing effect exhibited by the thermal shrinkage of the outer portion 6 b 22 is produced at the boundary portion between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, thus effectively significantly reducing or preventing the occurrence of cracks at this boundary portion.

As discussed above, in the multilayer ceramic capacitor 1B of the second preferred embodiment, the Si content ratio in the boundary portion P1 of the outer portion 6 b 22 with the inner portion 6 b 21 and that in the surface layer portion P2 of the outer portion 6 b 22 close to the second principal surface 2 a 2 are preferably set to be higher than that in the thickness-direction central portion of the outer portion 6 b 22. This configuration is implemented preferably by setting a temperature and a gaseous atmosphere at which Si segregates from grain boundaries of ceramic particles in the step of firing the body 2.

More specifically, in the step of firing the body 2, by setting a temperature and a gaseous atmosphere at which Si segregates from grain boundaries of ceramic particles, in the outer portion 6 b 22 containing a greater amount of Si, the grain growth of ceramic particles is encouraged, and Si segregates from the grain boundaries of coarsened ceramic particles. Segregated Si moves along the grain boundaries of the ceramic particles and concentrates toward the boundary portion P1 and the surface layer portion P2. As a result, the Si content ratio in the boundary portion P1 and that in the surface layer portion P2 of the outer portion 6 b 22 become higher than that in the thickness-direction central portion of the outer portion 6 b 22.

The Si content ratio in the boundary portion P1 of the outer portion 6 b 22 with the inner portion 6 b 21 is preferably higher than that in the thickness-direction central portion of the outer portion 6 b 22, thus improving the adhesion force between the outer portion 6 b 22 and the inner portion 6 b 21. The reason for this may be as follows. Si which has moved along the grain boundaries of the ceramic particles as described above fills many small gaps at the interface between the outer portion 6 b 22 and the inner portion 6 b 21, thus coupling the outer portion 6 b 22 and the inner portion 6 b 21 to each other. Accordingly, if the formation of the inner portion 6 b 21 and the formation of the outer portion 6 b 22 are separately performed, small gaps may be created at the interface between the inner portion 6 b 21 and the outer portion 6 b 22, and the concentration of segregated Si in the boundary portion P1 may be encouraged, thus enhancing the adhesion force between the outer portion 6 b 22 and the inner portion 6 b 21.

The Si content ratio in the surface layer portion P2 of the outer portion 6 b 22 close to the second principal surface 2 a 2 is preferably higher than that in the thickness-direction central portion of the outer portion 6 b 22, thus reducing or preventing a decrease in the mechanical strength of the body 2 when forming the first and second outer electrodes 5 a and 5 b. In the formation of the first and second outer electrodes 5 a and 5 b, if glass components contained in the first and second outer electrodes 5 a and 5 b react with the ceramic dielectric material of the body 2, the mechanical strength of the body 2 is decreased. However, if the Si content ratio in the outer portion 6 b 22 is high, the reaction of glass components contained in the first and second outer electrodes 5 a and 5 b with the ceramic dielectric material of the body 2 is significantly reduced or prevented.

In each of the ceramic dielectric layers 3 and 9, if a rare earth compound is contained in a perovskite compound expressed by ABO₃, which is a principal component, the molar ratio of a rare earth element to Ti in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 is preferably higher than that in the ceramic dielectric layer 9 defining the outer portion 6 b 22. That is, the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 preferably contain a greater amount of rare earth element than the outer portion 6 b 22.

As a rare earth element, Dy, Gd, Y, or La may be added to improve the functions of the multilayer ceramic capacitor 1B. More specifically, by adding a rare earth element, it is possible to stabilize the capacitor temperature characteristics and to prolong the life of the multilayer ceramic capacitor 1B by maintaining the insulation resistance (IR) value even under a high-temperature load.

A rare earth element is likely to concentrate in a grain boundary of ceramic particles or a segregation layer and also to elute to water-soluble flux. Accordingly, when mounting the multilayer ceramic capacitor 1B, ceramic components containing a rare earth element may elute to an organic acid, such as adipic acid, contained in water-soluble flux used for soldering. In this case, cracks may occur in an outer layer section of the body 2 which is embrittled as a result of the eluting of ceramic components.

Accordingly, the molar ratio of a rare earth element to Ti in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 is preferably about 0.003 mol or higher, and the molar ratio of a rare earth element to Ti in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is preferably lower than about 0.003 mol, for example. With this configuration, it is possible to stabilize the capacitor temperature characteristics and to prolong the life of the multilayer ceramic capacitor 1B by maintaining the insulation resistance (IR) value even under a high-temperature load, and also to significantly reduce or prevent the occurrence of cracks in the outer portion 6 b 22, which would be caused by the embrittlement of the outer portion 6 b 22 as a result of the eluting of ceramic components from the outer portion 6 b 22.

Although a detailed explanation is omitted, it has been validated, as a result of conducting verification tests (different from first through third verification tests, which will be discussed later) by changing the content of Dy used as a rare earth element, that the above-described advantages were obtained due to the above-described characteristic points. It has also been validated that the advantages were also obtained when Gd, Y, or La was used instead of Dy, for example.

In each of the ceramic dielectric layers 3 and 9, if a Mn compound is contained in a perovskite compound expressed by ABO₃, which is a principal component, the molar ratio of a Mn compound to Ti in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 is preferably higher than that in the ceramic dielectric layer 9 defining the outer portion 6 b 22. That is, the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 preferably contain a greater amount of Mn than the outer portion 6 b 22.

The color of a ceramic dielectric layer containing a smaller amount of Mn is lighter than that containing a greater amount of Mn. With this configuration, the color of the outer portion 6 b 22 is made brighter than that of the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21. It is thus easy to visually distinguish the first and second principal surfaces 2 a 1 and 2 a 2 of the multilayer ceramic capacitor 1B from each other.

Accordingly, by performing image processing by capturing an image of the multilayer ceramic capacitor 1B with an imaging camera, the orientation of the multilayer ceramic capacitor 1B in the thickness direction T is capable of being identified. Thus, when mounting the multilayer ceramic capacitor 1B, the orientation of the multilayer ceramic capacitor 1B is capable of being automatically identified so that the second principal surface 2 a 2 will face a mounting member, such as the wiring board 101.

For example, the molar ratio of Mn to Ti in the ceramic dielectric layers 3 defining the thickness-direction inner layer section 6 a, the thickness-direction first outer layer section 6 b 1, and the inner portion 6 b 21 is preferably about 0.0008 mol or higher, and the molar ratio of Mn to Ti in the ceramic dielectric layer 9 defining the outer portion 6 b 22 is preferably lower than about 0.0008 mol, for example.

Although a detailed explanation is omitted, it has been validated, as a result of conducting verification tests (different from first through third verification tests, which will be discussed later) by changing the content of Mn, that the above-described advantages were obtained due to the above-described characteristic points.

The multilayer ceramic capacitor 1B of the second preferred embodiment may also be mounted on a mounting member or integrated into a multilayer ceramic capacitor array, in a manner similar to the multilayer ceramic capacitor 1A of the first preferred embodiment.

First Verification Test

FIG. 18 is a table illustrating design conditions and evaluation results for multilayer ceramic capacitors of examples 1 through 21 in a first verification test.

In the first verification test, multilayer ceramic capacitors including a thickness-direction second outer layer section constituted by an inner layer and an outer layer, as discussed in the second preferred embodiment, were fabricated. Then, the occurrence of cracks in the body of each of the multilayer ceramic capacitors and the reliability of the multilayer ceramic capacitors after being subjected to firing were checked by changing the dimensions of the inner layer and the outer layer in the thickness direction and by changing the content of Si in each of the inner layer and the outer layer.

As shown in FIG. 18, in the first verification test, twenty samples of each of twenty-one types of multilayer ceramic capacitors of examples 1 through 21 were fabricated. The multilayer ceramic capacitors of examples 1 through 21 were all fabricated according to the non-limiting example of the manufacturing flow of the multilayer ceramic capacitor 1A discussed in the first preferred embodiment and were all configured as in the multilayer ceramic capacitor 1B of the second preferred embodiment. It is noted that all the dimensions in the table shown in FIG. 18 are indicated in terms of the design values.

In all of examples 1 through 21, the dimension t1 of the thickness-direction first outer layer section is about 40 μm, the dimension t2 of the thickness-direction second outer layer section is about 100 μm, and the dimension T1 of the multilayer unit in the thickness direction is about 620 μm.

In all of examples 1 through 21, the thickness x1 of each of inner electrode layers included in the multilayer unit subjected to firing is about 0.8 μm and the number of inner electrode layers stacked on each other is about 330. In all of examples 1 through 21, the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the inner layer (more specifically, the thickness-direction inner layer section, the thickness-direction first outer layer section, and the inner layer) is about 0.013 mol.

Concerning the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the outer layer of the thickness-direction second outer layer section, the molar ratio in examples 1 through 7 is about 0.017 mol, the molar ratio in examples 8 through 14 is about 0.029 mol, and the molar ratio in examples 15 through 21 is about 0.033 mol. The difference between the Si content in the ceramic dielectric layer defining the inner layer and that in the ceramic dielectric layer defining the outer layer in each of examples 1 through 21 is indicated in the table shown in FIG. 18.

Concerning the dimension t21 of the inner layer of the thickness-direction second outer layer section, in each of a group of examples 1 through 7, a group of examples 8 through 14, and a group of examples 15 through 21, the dimension t21 sequentially ranges from about 10 μm to 70 μm in increments of +10 μm.

Concerning the dimension t22 of the outer layer of the thickness-direction second outer layer section, in each of a group of examples 1 through 7, a group of examples 8 through 14, and a group of examples 15 through 21, the dimension t22 sequentially ranges from about 90 μm to 30 μm in increments of −10 μm.

In the first verification test, among the multilayer ceramic capacitors of examples 1 through 21 fabricated on the basis of the above-described design conditions, concerning ten samples of each of examples 1 through 21, after the body was subjected to firing, a W-T cross section including the center of the multilayer ceramic capacitor and parallel with both of the width direction and the thickness direction of each of the ten samples was exposed by polishing and was observed with an optical microscope so as to check for cracks. The remaining ten samples of each of examples 1 through 21 were input into a super-accelerating life tester so as to check the reliability of each of the ten samples. In this reliability test, a voltage of 8 V was continuously applied to each of the samples in an ambient temperature of 150° C., and then, the time taken for the IR value of each of the samples to reduce to 10 kΩ was measured.

Concerning the evaluation results of examples 1 through 21, if even one crack was found in the W-T cross sections of the ten samples of each of examples 1 through 21 after the body was subjected to firing, it was determined that cracks occurred (YES), and if none of cracks were found, it was determined that cracks did not occur (NO). Similarly, as a result of conducting the reliability test by inputting the ten samples of each of examples 1 through 21 into the super-accelerating life tester, if the time for the IR value of each of the samples to reduce to 10 kΩ was ten hours or longer, it was determined that the reliability was “GOOD”, and if the time for the IR value of each of the samples to reduce to 10 kΩ was shorter than ten hours, it was determined that the reliability was “BAD”.

As a result, as indicated in the evaluation results in FIG. 18, in examples 1 through 5, 8 through 12, and 15 through 19 in which the dimension t22 of the outer layer of the thickness-direction second outer layer section is equal to or greater than the dimension t21 of the inner layer of the thickness-direction second outer layer section, it was determined that cracks occurred neither in the samples subjected to firing nor in the samples subjected to the reliability test (NO). In all of examples 1 through 5, 8 through 12, and 15 through 19 in which it was determined that cracks did not occur (NO), it was determined that the reliability was “GOOD”, except for example 15 in which the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the outer layer was higher than about 0.029 mol and the dimension t21 of the inner layer was smaller than about 20 μm.

It is seen from the above-described results that cracks which may occur after the body is subjected to firing are effectively reduced or prevented if the dimension t22 of the outer layer of the thickness-direction second outer layer section is equal to or greater than the dimension t21 of the inner layer of the thickness-direction second outer layer section. It is also seen from the above-described results that, if the dimension t21 of the inner layer of the thickness-direction second outer layer section is about 20 μm or greater, for example, it is possible to significantly reduce or prevent the occurrence of the short-circuiting of the thickness-direction inner layer section by maintaining the withstand voltage characteristics of the ceramic dielectric layers included in the thickness-direction inner layer section.

Second Verification Test

FIG. 19 is a table illustrating design conditions and evaluation results for multilayer ceramic capacitors of examples through 25 in a second verification test. FIG. 20 is a schematic view illustrating a method for deflecting a wiring board having a multilayer ceramic capacitor mounted thereon in the second verification test.

In the second verification test, multilayer ceramic capacitors including a thickness-direction second outer layer section including an inner layer and an outer layer, as discussed in the second preferred embodiment, were fabricated. Then, the occurrence of cracks in the body of each of the multilayer ceramic capacitors after the application of an external stress was checked by changing the content of Si in each of the inner layer and the outer layer.

As shown in FIG. 19, in the second verification test, ten samples of each of four types of multilayer ceramic capacitors of examples 22 through 25 were fabricated. The multilayer ceramic capacitors of examples 22 through 25 were all fabricated according to the manufacturing flow of the multilayer ceramic capacitor 1A discussed in the first preferred embodiment and were all configured as in the multilayer ceramic capacitor 1B of the second preferred embodiment. It is noted that all the dimensions in the table shown in FIG. 19 are indicated in terms of the design values.

In all of examples 22 through 25, the dimension t1 of the thickness-direction first outer layer section is about 100 μm, the dimension t2 of the thickness-direction second outer layer section is about 100 μm, and the dimension T1 of the multilayer unit in the thickness direction is about 620 μm.

In all of examples 22 through 25, the dimension t21 of the inner layer of the thickness-direction second outer layer section is about 50 μm, and the dimension t22 of the outer layer of the thickness-direction second outer layer section is about 50 μm. The thickness x1 of each of inner electrode layers included in the multilayer unit subjected to firing is about 0.8 μm and the number of inner electrode layers stacked on each other is about 330.

Concerning the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the inner layer (more specifically, the ceramic dielectric layers defining the thickness-direction inner layer section, the thickness-direction first outer layer section, and the inner layer), the molar ratio in examples 22 and 24 is about 0.013 mol, the molar ratio in example 23 is about 0.017 mol, and the molar ratio in example 25 is about 0.029 mol.

Concerning the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the outer layer, the molar ratio in examples 22 and 23 is about 0.017 mol, and the molar ratio in examples 24 and 25 is about 0.029 mol. The difference between the Si content in the ceramic dielectric layer defining the inner layer and that in the ceramic dielectric layer defining the outer layer in each of examples 22 through 25 is indicated in the table shown in FIG. 19.

In the second verification test, concerning the ten samples of the multilayer ceramic capacitors of each of examples through 25 fabricated on the basis of the above-described design conditions, after the multilayer ceramic capacitors were mounted on respective mounting members and an external stress was applied to the mounting members, the occurrence of cracks reaching an inner electrode layer of each of the multilayer ceramic capacitors was checked.

In this case, the following method was used to apply an external stress to the mounting members, as shown in FIG. 20. A wiring board 101, which defines and serves as a mounting member, having the multilayer ceramic capacitor 1B mounted thereon was disposed such that the multilayer ceramic capacitor 1B faced downward. The wiring board 101 was supported at both sides by support members 301 from below. In this state, a pressing tool 300 was vertically pressed against the top surface of the wiring board 101 from upward toward the direction indicated by the arrow DR in FIG. 20 so as to deflect the wiring board 101 downward. By deflecting the wiring board 101 with this method, a tensile stress, which is an external stress, was applied to the multilayer ceramic capacitor 1B via solder and the first and second outer electrodes 5 a and 5 b.

After applying an external stress to the ten samples of the multilayer ceramic capacitors of each of examples 22 through 25 by using this method, the multilayer ceramic capacitors were demounted from the respective wiring boards. Then, cross sections of the multilayer ceramic capacitors of the ten samples were exposed by polishing and were observed with an optical microscope so as to check for cracks reaching an inner electrode layer.

Concerning the evaluation results of examples 22 through 25, as a result of observing the cross sections, if even one crack reaching an inner electrode layer was found in the cross sections of the ten samples of each of examples 22 through 25, it was determined that cracks occurred (YES), and if none of cracks reaching an inner electrode layer were found, it was determined that cracks did not occur (NO).

As a result, as indicated in the evaluation results in FIG. 19, in examples 22 and 24 in which the Si content in the ceramic dielectric layer defining the inner layer and that in the ceramic dielectric layer defining the outer layer differed from each other, it was determined that cracks reaching an inner electrode layer did not occur (NO), but on the other hand, in examples 23 and 25 in which the Si content in the ceramic dielectric layer defining the inner layer and that in the ceramic dielectric layer defining the outer layer did not differ from each other, it was determined that cracks reaching an inner electrode layer occurred (YES).

It is seen from the above-described results that, by setting the amount of Si content in the ceramic dielectric layer defining the outer layer to be higher than that in the ceramic dielectric layer defining the inner layer, a boundary portion having a higher Si content ratio is provided in the outer layer. As a result, the development of cracks is significantly reduced or prevented, or the direction in which cracks develop changes, thus preventing cracks from reaching an inner electrode layer.

Third Verification Test

In the third verification test, multilayer ceramic capacitors including a thickness-direction second outer layer section included an inner layer and an outer layer, as discussed in the second preferred embodiment, were fabricated. Then, the occurrence of cracks in the body of each of the multilayer ceramic capacitors after the body was subjected to firing was checked by changing the curving amount of first and second extension portions.

In the third verification test, twenty samples of each of two types of multilayer ceramic capacitors of examples 26 and were fabricated. The multilayer ceramic capacitors of examples 26 and 27 were all fabricated according to the manufacturing flow of the multilayer ceramic capacitor 1A discussed in the first preferred embodiment and were all configured as in the multilayer ceramic capacitor 1B of the second preferred embodiment. It is noted that all the dimensions discussed in the third verification test are indicated in terms of the design values.

In both of examples 26 and 27, the dimension t1 of the thickness-direction first outer layer section is about 40 μm, the dimension t2 of the thickness-direction second outer layer section is about 150 μm, and the dimension T1 of the multilayer unit in the thickness direction is about 620 μm.

In both of examples 26 and 27, the dimension t21 of the inner layer of the thickness-direction second outer layer section is about 90 μm, and the dimension t22 of the outer layer of the thickness-direction second outer layer section is about 60 μm.

In both of examples 26 and 27, the thickness x1 of each of inner electrode layers included in the multilayer unit subjected to firing is about 0.8 μm and the number of inner electrode layers stacked on each other is about 330.

In both of examples 26 and 27, the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the inner layer (more specifically, the ceramic dielectric layers defining the thickness-direction inner layer section, the thickness-direction first outer layer section, and the inner layer) is about 0.013 mol, while the molar ratio of Si to Ti contained in the ceramic dielectric layer defining the outer layer is about 0.029 mol.

In example 26, among a plurality of inner electrode layers stacked in the thickness direction, the widthwise dimension of inner electrode layers positioned toward the thickness-direction second outer layer section is gradually decreased as the inner electrode layers are closer to the second principal surface. Additionally, the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction second outer layer section is preferably set to be greater than the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction first outer layer section.

The multilayer ceramic capacitor configured as described above was manufactured by sequentially stacking material sheets starting from a material sheet which will form the first principal surface. The largest dimension of the inner electrode layer in the width direction (the dimension of an inner electrode layer positioned closer to the thickness-direction first outer layer section) is about 620 μm, while the smallest dimension of the inner electrode layer in the width direction (the dimension of the second conductive layer positioned closest to the thickness-direction second outer layer section) is about 600 μm.

In example 27, among a plurality of inner electrode layers stacked in the thickness direction, the widthwise dimension of inner electrode layers positioned toward the thickness-direction first outer layer section is gradually decreased as the inner electrode layers are closer to the first principal surface. Additionally, the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction first outer layer section is set to be greater than the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction second outer layer section.

The multilayer ceramic capacitor configured as described above was manufactured by sequentially stacking material sheets starting from a material sheet which will form the second principal surface. The largest dimension of the inner electrode layer in the width direction (the dimension of an inner electrode layer positioned closer to the thickness-direction second outer layer section) is about 620 μm, while the smallest dimension of the inner electrode layer in the width direction (the dimension of the first conductive layer positioned closest to the thickness-direction first outer layer section) is about 600 μm.

In the third verification test, concerning twenty samples of each of examples 26 and 27, after the body was subjected to firing, a W-T cross section including the center of the multilayer ceramic capacitor and parallel with both of the width direction and the thickness direction was exposed by polishing and was observed with an optical microscope so as to check for cracks. Thereafter, an L-T cross section including the center of the multilayer ceramic capacitor and parallel with both of the length direction and the thickness direction was exposed by polishing and was observed with an optical microscope so as to check for cracks.

Concerning the evaluation results of examples 26 and 27, if even one crack was found in the W-T and L-T cross sections of the twenty samples of each of examples 26 and 27 after the body was subjected to firing, it was determined that cracks occurred (YES), and if none of cracks were found, it was determined that cracks did not occur (NO).

As a result, concerning example 26, it was determined that cracks occurred neither in the W-T cross section nor in the L-T cross section (NO), while concerning example 27, it was determined that cracks occurred both in the W-T cross section and in the L-T cross section (YES).

The above-described results show that, concerning the length direction, the occurrence of cracks is effectively reduced or prevented if the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction second outer layer section is preferably set to be greater than the curving amount of the first and second extension portions included in the inner electrode layers positioned toward the thickness-direction first outer layer section. The above-described results also show that, concerning the width direction, the occurrence of cracks is effectively reduced or prevented if, among a plurality of inner electrode layers stacked in the thickness direction, the widthwise dimension of inner electrode layers positioned toward the thickness-direction second outer layer section is gradually decreased as the inner electrode layers are closer to the second principal surface.

Measurement methods for dimensions of individual sections of a multilayer ceramic capacitor will be discussed below.

FIG. 21 illustrates an example of an enlarged image of a cross section of a multilayer ceramic capacitor observed with a scanning electron microscope (SEM). In FIG. 21, a portion of the second principal surface 2 a 2 of the multilayer ceramic capacitor in contact with an embedding resin 400 is shown.

When measuring the thickness of a ceramic dielectric layer 3 and a conductive layer (inner electrode layer) 4 of a multilayer ceramic capacitor, the following method is preferably used. In an enlarged image of a cross section of the multilayer ceramic capacitor observed with a SEM, as shown in FIG. 21, a straight line Lc extending in the thickness direction of a body of the multilayer ceramic capacitor and passing through the center of the body is drawn. Then, a plurality of straight lines parallel with the straight line Lc are drawn at equal pitches S. The pitch S may be set to be about five to ten times as long as the thickness of the ceramic dielectric layer 3 or that of the conductive layer 4 to be measured, for example. If, for example, the ceramic dielectric layer 3 having a thickness of about 1 μm is measured, the pitch S preferably is set to be about 5 μm. Then, lines are drawn on both sides of the straight line Lc. The number of lines drawn on one side and that on the other side of the straight line Lc are the same. That is, an odd number of lines including the straight line Lc are drawn. In FIG. 21, an example in which five straight lines La through Le are drawn is shown.

Then, on each of the lines La through Le, the thickness of a ceramic dielectric layer 3 and that of a conductive layer 4 are measured. If, on each of the straight lines La through Le, a conductive layer 4 is partially missing and ceramic dielectric layers 3 join each other with the conductive layer 4 therebetween, or if an enlarged image at a portion to be measured is not clear, the thickness or the distance is measured on another straight line separated from the straight line Lc.

When measuring the thickness of a ceramic dielectric layer 3, as shown in FIG. 21, the thickness D1 on the straight line La, the thickness D2 on the straight line Lb, the thickness D3 on the straight line Lc, the thickness D4 on the straight line Ld, and the thickness D5 on the straight line Le are measured, and the average value thereof is set to be the thickness of the ceramic dielectric layer 3.

When calculating the average thickness of a plurality of ceramic dielectric layers included in a multilayer unit, the thicknesses of a total of five ceramic dielectric layers constituted by the ceramic dielectric layer positioned substantially at the center of the multilayer unit in the thickness direction and two ceramic dielectric layers positioned at each of both sides of this ceramic dielectric layer are measured by using the above-described method, and the average value thereof is set to be the average thickness of the plurality of ceramic dielectric layers included in the multilayer unit.

If the number of ceramic dielectric layers stacked on each other is less than five, the thicknesses of all the ceramic dielectric layers are measured by using the above-described method, and the average value thereof is set to be the average thickness of the ceramic dielectric layers. If the number of conductive layers stacked on each other is less than five, the thicknesses of all the conductive layers are measured by using the above-described method, and the average value thereof is set to be the average thickness of the conductive layers.

An example of the method for measuring the dimensions of the width-direction first and second outer layer sections is as follows. A W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the widthwise dimension of a portion adjacent to the conductive layer positioned closest to the first principal surface and/or the widthwise dimension of a portion adjacent to the conductive layer positioned closest to the second principal surface are measured.

An example of the method for measuring the dimensions of the length-direction first and second outer layer sections is as follows. An L-T cross section including the center of the body and parallel with both of the length direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the longitudinal dimension of a portion adjacent to the conductive layer positioned closest to the first principal surface and/or the longitudinal dimension of a portion adjacent to the conductive layer positioned closest to the second principal surface are measured.

An example of the method for measuring the curving amount of the extension portions of the first outermost layer is as follows. An L-T cross section including the center of the body and parallel with both of the length direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the thickness-direction distance between the position of the first outermost layer at the center of the body in the width direction and the position of the first outermost layer connected to the external electrode is measured.

An example of the method for measuring the curving amount of the extension portions of the second outermost layer is as follows. An L-T cross section including the center of the body and parallel with both of the length direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the thickness-direction distance between the position of the second outermost layer at the center of the body in the width direction and the position of the second outermost layer connected to the external electrode is measured.

An example of the method for measuring the dimension of the multilayer unit in the width direction is as follows. A W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the largest dimension of the conductive layer in the width direction is measured.

An example of the method for measuring the dimension of the multilayer unit in the thickness direction is as follows. A W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the length of the shortest line segment including the center of the body and connecting the conductive layer positioned closest to the first principal surface and the conductive layer positioned closest to the second principal surface is measured as the dimension of the multilayer unit in the thickness direction.

The widthwise dimension of the conductive layer positioned closest to the first principal surface and the widthwise dimension of the conductive layer positioned closest to the second principal surface may be measured by exposing a W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction by polishing and by observing the W-T cross section with an optical microscope.

The widthwise dimension of the conductive layer positioned at the center of the multilayer unit in the thickness direction may be measured by exposing a W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction by polishing and by observing the W-T cross section with an optical microscope.

An example of the method for measuring the dimensions of the thickness-direction first and second outer layer sections and the dimensions of the inner layer and the outer layer of the thickness-direction second outer layer section is as follows. A W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction is exposed by polishing and is observed with an optical microscope. Then, the thicknesses of the thickness-direction first and second outer layer sections and those of the inner layer and the outer layer of the thickness-direction second outer layer section substantially at the center of the body in the width direction are measured.

The areas S1 and S2 may be measured preferably by exposing a W-T cross section including the center of the body and parallel with both of the width direction and the thickness direction by polishing and by observing the W-T cross section with an optical microscope.

Analysis methods for the compositions of the individual sections of a multilayer ceramic capacitor will be described below.

Analysis for the composition of components contained in ceramic dielectric layers may be conducted by using inductively coupled plasma (ICP) emission spectrometry or a WDX, for example. If elemental analysis is conducted by using ICP emission spectrometry, a sample is formed into a powder and is dissolved with an acid. Then, the resulting solution is subjected to ICP emission spectrometry, thereby specifying the composition. If elemental analysis is conducted by using a WDX, the above-described W-T cross section is exposed by polishing the body embedded in a resin, and then, the composition is specified by using a WDX attached to a SEM.

The above-described boundary portion of the outer layer having a high Si content may be identified as follows. The above-described W-T cross section is exposed by polishing the body embedded in a resin, and a backscattered electron image of the exposed cross section is captured by using a SEM and is observed. Alternatively, the boundary portion may be identified by creating element mapping of the exposed cross section by using a WDX attached to a SEM and by specifying a portion having a high Si content.

In the above-described first and second preferred embodiments of the present invention, the first and second outermost layers 4 a and 4 b are connected to different outer electrodes, that is, to the first and second outer electrodes 5 a and 5 b, respectively. However, both of the first and second outermost layers 4 a and 4 b may be connected to one of the first and second outer electrodes 5 a and 5 b. In this case, the curving amounts of the extension portions of the first and second outermost layers 4 a and 4 b is determined by one of the curving state in the length-direction first outer layer section 7 b 1 and that in the length-direction second outer layer section 7 b 2.

In the above-described first and second preferred embodiments of the present invention, in the above-described specific cross sections, for example, the cross sections shown in FIGS. 3, 6, 7A, 7B, and 17, the multilayer unit 10 is configured such that a rectangle and a trapezoid preferably are connected to each other (one side of the rectangle and the longer side of a pair of parallel sides of the trapezoid join each other), for example. However, it is not always necessary that the multilayer unit 10 is configured in this shape. The multilayer unit 10 may be configured in another shape as long as the widthwise dimension we2 of the second conductive layer 4 b disposed closest to the second principal surface 2 a 2 is smaller than the widthwise dimension we3 of the central inner electrode layer 4 c, which defines and serves as the third conductive layer, positioned closest to the central portion of the multilayer unit 10 in the thickness direction T.

Cracks may occur in a boundary between the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1, though the possibility of the occurrence of cracks in this boundary is smaller than that between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2. Accordingly, in order to reduce the occurrence of cracks between the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1, the widthwise dimension of a portion of the multilayer unit 10 positioned toward the thickness-direction first outer layer section 6 b 1 may be set to be smaller, by a certain degree, than that of the multilayer unit 10 positioned at the central portion of the multilayer unit 10 in the thickness direction T. Typically, among the plurality of inner electrode layers 4 stacked on each other in the thickness direction T, the widthwise dimension of inner electrode layers 4 positioned toward the thickness-direction first outer layer section 6 b 1 may be gradually decreased as the inner electrode layers 4 are closer to the first principal surface 2 a 1. In this case, the multilayer unit 10 is configured generally in a hexagonal shape in which two trapezoids are connected to each other with the thickness-direction central portion of the multilayer unit 10 therebetween (the longer side of a pair of parallel sides of one trapezoid joins that of the other trapezoid).

With this configuration, it is possible to effectively reduce or prevent the occurrence of cracks, not only in the boundary between the thickness-direction inner layer section 6 a and the thickness-direction second outer layer section 6 b 2, but also in the boundary between the thickness-direction inner layer section 6 a and the thickness-direction first outer layer section 6 b 1.

In the above-described first and second preferred embodiments of the present invention, in order to reduce or prevent the occurrence of cracks in the width direction W, the widths of some inner electrode layers 4 are different, and more specifically, among the plurality of inner electrode layers 4 stacked on each other in the thickness direction T, the widthwise dimension of inner electrode layers 4 positioned toward the thickness-direction second outer layer section 6 b 2 is gradually decreased as the inner electrode layers 4 are closer to the second principal surface 2 a 2. However, from the viewpoint of reducing or preventing the occurrence of cracks in the length direction L, it is not always necessary that the multilayer unit 10 be configured in this manner. Instead, the multilayer unit 10 may have a substantially rectangular parallelepiped shape.

While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing from the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims. 

What is claimed is:
 1. A multilayer ceramic capacitor comprising: a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction; and a plurality of outer electrodes disposed on portions of the body; wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction; the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface; some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode; the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween; the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections; a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction; one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface; one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface; and an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer.
 2. The multilayer ceramic capacitor according to claim 1, wherein a dimension of the second outermost conductive layer in the width direction is smaller than a dimension of a third conductive layer in the width direction which is disposed closest to a center of the multilayer unit in the thickness direction.
 3. The multilayer ceramic capacitor according to claim 1, wherein the ceramic dielectric layers included in the thickness-direction inner layer section and the thickness-direction first and second outer layer sections contains barium titanate and Si; the thickness-direction second outer layer section includes an outer portion which defines the second principal surface and an inner portion disposed between the thickness-direction inner layer section and the outer portion; a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the outer portion is higher than a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the inner portion; and a boundary portion disposed between the outer portion and the inner portion has a larger Si content than the outer portion.
 4. The multilayer ceramic capacitor according to claim 3, wherein the ceramic dielectric layers included in the multilayer unit have a higher composition ratio of rare earth element to Ti than the outer portion; and the inner portion has a higher composition ratio of Mn to Ti than that of the outer portion.
 5. The multilayer ceramic capacitor according to claim 3, wherein a dimension of the outer portion in the thickness direction is greater than a dimension of the inner portion in the thickness direction.
 6. The multilayer ceramic capacitor according to claim 1, wherein a dimension of the multilayer unit in the thickness direction is greater than a dimension of the multilayer unit in the width direction; and a dimension of the body in the thickness direction is greater than a dimension of the body in the width direction.
 7. A multilayer ceramic capacitor comprising: a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction; and a plurality of outer electrodes disposed on portions of the body; wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction; the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface; some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode; the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween; the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections; a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction; one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface; one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface; an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer; the second outermost conductive layer is an ineffective conductive layer; and the amount of the inclination of the second outermost conductive layer is larger than a thickness of the ceramic dielectric layer adjacent to the second outermost conductive layer in the multilayer unit.
 8. The multilayer ceramic capacitor according to claim 7, wherein a dimension of the second outermost conductive layer in the width direction is smaller than a dimension of a third conductive layer in the width direction which is disposed closest to a center of the multilayer unit in the thickness direction.
 9. The multilayer ceramic capacitor according to claim 7, wherein the ceramic dielectric layers included in the thickness-direction inner layer section and the thickness-direction first and second outer layer sections contains barium titanate and Si; the thickness-direction second outer layer section includes an outer portion which defines the second principal surface and an inner portion disposed between the thickness-direction inner layer section and the outer portion; a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the outer portion is higher than a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the inner portion; and a boundary portion disposed between the outer portion and the inner portion has a larger Si content than the outer portion.
 10. The multilayer ceramic capacitor according to claim 9, wherein the ceramic dielectric layers included in the multilayer unit have a higher composition ratio of rare earth element to Ti than the outer portion; and the inner portion has a higher composition ratio of Mn to Ti than that of the outer portion.
 11. The multilayer ceramic capacitor according to claim 9, wherein a dimension of the outer portion in the thickness direction is greater than a dimension of the inner portion in the thickness direction.
 12. The multilayer ceramic capacitor according to claim 7, wherein a dimension of the multilayer unit in the thickness direction is greater than a dimension of the multilayer unit in the width direction; and a dimension of the body in the thickness direction is greater than a dimension of the body in the width direction.
 13. A multilayer ceramic capacitor comprising: a body including conductive layers and ceramic dielectric layers alternately stacked on each other in a thickness direction; and a plurality of outer electrodes disposed on portions of the body; wherein the body includes first and second principal surfaces opposing each other in the thickness direction, first and second end surfaces opposing each other in a length direction, and first and second side surfaces opposing each other in a width direction; the plurality of outer electrodes includes a first outer electrode covering at least the first end surface and a second outer electrode covering at least the second end surface; some of the conductive layers include a first effective portion and a first extension portion extending from the first effective portion toward the first end surface and connecting to the first outer electrode, and others of the conductive layers include a second effective portion and a second extension portion extending from the second effective portion toward the second end surface and connecting to the second outer electrode; the body includes a multilayer unit including an effective portion defined by the first and second effective portions and portions of the ceramic dielectric layers stacked therebetween; the body includes a thickness-direction first outer layer section that includes one of the ceramic dielectric layers and that defines the first principal surface, a thickness-direction second outer layer section that includes another of the ceramic dielectric layers and that defines the second principal surface, and a thickness-direction inner layer section that includes the multilayer unit and that is disposed between the thickness-direction first and second outer layer sections; a dimension of the thickness-direction second outer layer section in the thickness direction is greater than a dimension of the thickness-direction first outer layer section in the thickness direction; one of the first and second extension portions of a first outermost conductive layer of the conductive layers that is closest to the first principal surface is inclined toward the second principal surface; one of the first and second extension portions of a second outermost conductive layer of the conductive layers that is closest to the second principal surface is inclined toward the first principal surface; an amount of inclination of the second outermost conductive layer is greater than an amount of inclination of the first outermost conductive layer; the conductive layer nearest to the first principal surface is a first conductive layer; a distance between the multilayer unit and the first side surface through the first conductive layer in the width direction and a distance between the multilayer unit and the second side surface through the first conductive layer in the width direction are greater than a dimension of the thickness-direction first outer layer section in the thickness direction; and a distance between the multilayer unit and the first end surface through the first conductive layer in the length direction and a distance between the multilayer unit and the second end surface through the first conductive layer in the length direction are greater than a dimension of the thickness-direction first outer layer section in the thickness direction.
 14. The multilayer ceramic capacitor according to claim 13, wherein a dimension of the second outermost conductive layer in the width direction is smaller than a dimension of a third conductive layer in the width direction which is disposed closest to a center of the multilayer unit in the thickness direction.
 15. The multilayer ceramic capacitor according to claim 13, wherein the ceramic dielectric layers included in the thickness-direction inner layer section and the thickness-direction first and second outer layer sections contains barium titanate and Si; the thickness-direction second outer layer section includes an outer portion which defines the second principal surface and an inner portion disposed between the thickness-direction inner layer section and the outer portion; a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the outer portion is higher than a composition ratio of Si to Ti in one of the ceramic dielectric layers included in the inner portion; and a boundary portion disposed between the outer portion and the inner portion has a larger Si content than the outer portion.
 16. The multilayer ceramic capacitor according to claim 15, wherein the ceramic dielectric layers included in the multilayer unit have a higher composition ratio of rare earth element to Ti than the outer portion; and the inner portion has a higher composition ratio of Mn to Ti than that of the outer portion.
 17. The multilayer ceramic capacitor according to claim 15, wherein a dimension of the outer portion in the thickness direction is greater than a dimension of the inner portion in the thickness direction.
 18. The multilayer ceramic capacitor according to claim 13, wherein a dimension of the multilayer unit in the thickness direction is greater than a dimension of the multilayer unit in the width direction; and a dimension of the body in the thickness direction is greater than a dimension of the body in the width direction. 